Polymer Resources PC-FR-UV-10-0002-16A Polycarbonate, Flame Retardant, Medium Flow
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC-FR-UV-10-0002-16A Polycarbonate, Flame Retardant, Medium Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, Flame Retardant, Medium FlowFeatures: • Ultra High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 - 16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 22.8 °C |
15.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 266 - 288 °C | 510 - 550 °F | |
| Middle Barrel Temperature | 277 - 299 °C | 530 - 570 °F | |
| Front Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Melt Temperature | 282 - 310 °C | 540 - 590 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Permabond F202 Anaerobic Retainer
- PolyOne Edgetek® NL-50GF/000 Black 13 Nylon 6/12, Glass Filled (discontinued **)
- Ineos Nova T243C Expandable Polystyrene
- Samsung Cheil Industries Starex® AS-0151BS ABS, Unreinforced
- Engineered Syntactic Systems BZ-28 Deep Water Syntactic Foam
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=6.5, Diameter 0.4 mm)
- DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6 (Unverified Data**)
- BASF Triethanolamine Pure
- Bapolene® 4082 Polypropylene, Injection Grade
- ExxonMobil Santoprene® 8271-80HT Thermoplastic Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved