Multibase Multi-Flex® TPE A 7606 BLK
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPE A 7606 BLK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | (Condition L) ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | 10 sec; ASTM D-2240 |
| Tensile Strength, Ultimate | >= 7.45 MPa | >= 1080 psi | ASTM D412 |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D412 |
| Tear Strength | >= 24.5 kN/m | >= 140 pli | ASTM D624 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD171R PC (Europe-Africa-Middle East)
- LG Chemical Phenol
- Sylvin Technologies 8950-75 Natural PVC Extrusion Compound
- Shakespeare WN-102 diameter 0.5 mm Nylon 66 Monofilament
- A. Schulman POLYBATCH™ White L8350 HSF Concentrate Based In High-Flow LLDPE
- Dalau Dalcon 018 85% Virgin PTFE, 15% Graphite
- DuPont Elvanol® 70-27 Polyvinyl Alcohol Intermediately Hydrolyzed General Purpose Grade
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N990 Filler
- PlastxWorld CEVIAN®-V T150 ABS
Copyright © lookpolymers.com All Rights Reserved