Polymer Resources NY66-IM2-[color]H Nylon, Superior Impact Modified, Heat Stabilized (DAM)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources NY66-IM2-[color]H Nylon, Superior Impact Modified, Heat Stabilized (DAM).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³	ASTM D792
Linear Mold Shrinkage	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	51.7 MPa	7500 psi	ASTM D638
Tensile Strength, Yield	50.3 MPa	7300 psi	ASTM D638
Flexural Strength	62.1 MPa	9000 psi	ASTM D790
Flexural Modulus	1.69 GPa	245 ksi	ASTM D790
Izod Impact, Notched	8.54 J/cm	16.0 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	213 °C	415 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	68.3 °C	155 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in

Processing Properties	Metric	English
Rear Barrel Temperature	266 - 277 °C	510 - 530 °F
Middle Barrel Temperature	271 - 282 °C	520 - 540 °F
Front Barrel Temperature	277 - 288 °C	530 - 550 °F
Melt Temperature	277 - 293 °C	530 - 560 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	73.9 - 85.0 °C	165 - 185 °F
Dry Time	3 - 4 hour	3 - 4 hour