Polykemi AB POLYfill PP CIP6020F Polypropylene, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP CIP6020F Polypropylene, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | With Flow; ISO 2577 |
| 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 21.0 MPa | <= 3050 psi | ISO/R527 |
| Flexural Strength | <= 35.0 MPa | <= 5080 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
ISO 179 |
| 0.350 J/cm² @Temperature -20.0 °C |
1.67 ft-lb/in² @Temperature -4.00 °F |
ISO 179 | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 66.0 °C @Load 5.001 kg |
151 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 145 °C @Load 1.00 kg |
293 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 70.0 MPa | 5800 - 10200 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | < 20 | % of injection pressure |
| Injection Speed () | Medium |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 120 Aramid Reinforced
- Radici Radilon® N66-SRV130 Nylon 66 (discontinued **)
- Fiberfil® J-69/30/E/M High performance polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
- Ipiranga Petrochem GM 7746 A HDPE
- Schwartz Technical Plastics LAMIGAMID® 700 Ultra High Molecular Weight Polyethylene
- Shandong Dongyue Polymer DF-11 PTFE Molding Powder (Micronized Particles)
- Eurotec® Tecomid® NB40 KK40 NL PA6, 40% glass fiber/mineral reinforced, natural
- Arlon 44560R009 0.009" (0.229 mm) Uncured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66
- EMS-Grivory Grivory® F 50 nat 6368 PA6
Copyright © lookpolymers.com All Rights Reserved