Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polycasa XT 610 PMMA

Category Polymer , Thermoplastic , Acrylic (PMMA)
Manufacturer Polycasa
Trade Name XT
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polycasa XT 610 PMMA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
QUINN XT sheets have good optical properties and a brilliant surface. QUINN XT sheets offer excellent transparency, good mechanical properties, are UV resistant, have very good weathering and ageing resistance and remain color constant for years. High impact grades, QUINN XT610, XT620, XT630, have outstanding mechanical properties and excellent impact strength. Both QUINN XT sheets and all high impact grades can be used in contact with foodstuffs, as they meet all current European food control legislation. QUINN XT sheets and the high impact grades do not contain any toxic materials or heavy metals, which may cause environmental damage or health risks. It is insoluble in water, and not subject to hazardous materials identification. QUINN XT sheets and the high impact grades are easy to recycle.Construction Components Light domes Partition walls Door Glazing Roofing Skylights for caravans Lighting Lighting control lensesDomestic light fittings Engineering ComponentsMachine housings, machine safety covers Advertising and SignageMolded lettersStore displaysShop fittingsIlluminated graphics panels Other ApplicationsContainersLettering TemplatesSolariumsSound Barrier WallsQuinn Manufacturing Group rebranded its Plastics Division as Polycasa in 2013.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
24h/23°C - 50x50x4mm; DIN 53495 Method 1
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Mechanical Properties Metric English Comments
Ball Indentation Hardness 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
ISO 527-2
Elongation at Break 35 %
35 %
ISO 527-2
Tensile Modulus 1.80 GPa
261 ksi
ISO 527-2
Flexural Strength 65.0 MPa
9430 psi
ISO 178
Flexural Modulus 1.80 GPa
261 ksi
ISO 178
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
IEC 1006
Thermal Conductivity 0.180 W/m-K
1.25 BTU-in/hr-ft²-°F
DIN 52612
Maximum Service Temperature, Air 65.0 °C
149 °F
Continuous Use
75.0 °C
167 °F
Short Term Use
Vicat Softening Point 98.0 °C
208 °F
ISO 306
Decomposition Temperature >= 280 °C
>= 536 °F
Optical Properties Metric English Comments
Refractive Index 1.492
1.492
DIN 5036-3
Transmission, Visible 90 %

@Thickness 3.00 mm
90 %

@Thickness 0.118 in
DIN 5036-3
Electrical Properties Metric English Comments
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
DIN 53481
Dissipation Factor 0.030

@Frequency 1e+6 Hz
0.030

@Frequency 1e+6 Hz
DIN 53483-2
Descriptive Properties Value Comments
Forming Temperature, Air Pressure, °C 130-150
Forming Temperature, Vacuum, °C 140-170