Aclo Accutech Polypropylene Homopolymer HP0336M10L Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336M10L Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched | 0.448 J/cm | 0.840 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
Users viewing this material also viewed the following:
- MV Labs EU1000 Eu2(SO4)3·8H2O Europium(III) sulfate octahydrate
- MarkeTech Cu/Mo/Cu 1:2:1 Laminated Sheet
- Lord Adhesives 8601 Polymer Resistor Composition
- Solvay Specialty Polymers Halar® 6014 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Covestro Baydur® GS-772 Polyurethane Solid RIM, MDI-based 2-Component Liquid System
- API Megol AM DP2392/32 SEBS Adhesion Modified Overmolding for Polar Polymers
- Axiall 34551 Wire & Cable Flexible PVC
- Parker Chomerics CHO-FORM 5541 Conductive Form-In-Place Gaskets
- Buckeye Polymers BP RPP 2520 CU Polypropylene, 25% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved