Chi Mei Kibiton® PB-5925 SBC
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Kibiton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Kibiton® PB-5925 SBC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparency, high stiffness, injection grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
11 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | |
| Tensile Strength at Break | 19.0 MPa | 2760 psi | 50 mm/min, 4 mm; ISO 527 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min, 4 mm; ISO 527 |
| Elongation at Break | 43 % | 43 % | 50 mm/min, 4mm; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 50 mm/min, 4 mm; ISO 527 |
| Flexural Strength | 43.0 MPa | 6240 psi | 2 mm/min, 4 mm; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min, 4 mm; ISO 178 |
| Izod Impact, Notched | 0.246 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.460 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Notched (ISO) | 2.30 kJ/m² | 1.09 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.260 J/cm² | 1.24 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | unannealed; ISO 75 |
| 83.0 °C | 181 °F | annealed; ISO 75 | |
| Vicat Softening Point | 73.0 °C @Load 5.00 kg |
163 °F @Load 11.0 lb |
120°C/hr; ISO 306 |
| 75.0 °C @Load 5.00 kg |
167 °F @Load 11.0 lb |
50°C/hr; ISO 306 | |
| 92.0 °C @Load 1.00 kg |
198 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| 95.0 °C @Load 1.00 kg |
203 °F @Load 2.20 lb |
50°C/hr; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.5 % @Thickness 3.17 mm |
2.5 % @Thickness 0.125 in |
ASTM D1003 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 66 BT B 27 A/IM PA66
- NEXA® PFX8050 Perfluoroelastomer
- Polymer Resources PPX-G10HF Modified-PPO, 10% Glass Reinforced, High Flow
- SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI (Europe-Africa-Middle East)
- Struktol STRUKSILON 8030 Silicone Stabilizer for PU-Rigid Foam
- DuPont Performance Polymers Hytrel® 8238 Polyester Elastomer TPC-ET (Unverified Data**)
- 3M 363L Specialty Foil Tape
- Asahi Kasei Tenac®-C 7520 Copolymer Acetal Resin
- 3M FV033 Indoor UL Recognized White Vinyl Label Products
- LATI Latiblend 6252 H2 G/30 PA6/PP Homopolymer
Copyright © lookpolymers.com All Rights Reserved