- PolyOne Lubri-Tech™ PS-15GB/10T Polybutylene Terephthalate (PBT), Glass Bead Filled, PTFE Lubricated (discont
PolyOne Lubri-Tech™ PS-15GB/10T Polybutylene Terephthalate (PBT), Glass Bead Filled, PTFE Lubricated (discont
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PS-15GB/10T Polybutylene Terephthalate (PBT), Glass Bead Filled, PTFE Lubricated
(discont.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.485 g/cc | 1.485 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 46.2 MPa | 6700 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 271 °C | 480 - 520 °F | Molding |
| Mold Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Drying Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE ZS2606 Thermoplastic Elastomer, SEBS/SBS-based
- H.C. Starck Grade BF 17 Silicon Carbide, SiC
- SABIC Innovative Plastics NORYL FXN121BK PPE+HIPS
- A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
- Tipco Tipcolite® TPF 1111 - Rubber & Mineral Modified Phenolic Resin, 19 mm Norton Flow with 7% Hexamine
- Chengdu Polyster KP-400 Nucleating Masterbatch Special for PET
- Fainplast Compounds CKL 80/3 Flexible PVC, Sheathing Lead Free
- BASF Neopolen® P 9035 0.06 g/cc Core density; Expanded Polypropylene (Europe)
- Beijing Evergrow Resources PTFE, 60% Bronze Filled
- A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE
Copyright © lookpolymers.com All Rights Reserved