- PolyOne Edgetek® SF-40GF-10 MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled (discontinued **)
PolyOne Edgetek® SF-40GF-10 MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-40GF-10 MN/000 Polyphenylene Sulfide (PPS), Glass/Mineral Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass/Mineral ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.77 g/cc | 1.77 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Ultimate | 103 MPa | 15000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.2 µm/m-°C @Temperature 20.0 °C |
14.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.432 W/m-K | >= 3.00 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 282 °C | 540 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 510 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 299 - 332 °C | 570 - 630 °F | Molding |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-924 Impact Modified Acrylic Resin
- PolyOne Elastamax™ EG-9182 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Cycoloy® C1110 PC+ABS (Asia Pacific)
- ExxonMobil Escorene® LD 720.92 Specialty Film Resin (discontinued **)
- Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; H (TD04) Temper; over 9.5 to 25 mm Thickness (UNS C17200)
- SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp RW008XXZ PA 66
- ChevronTexaco HS Heating Fuel 2
- ExxonMobil Oppalyte™ 42MH648 OPP Film
- ExxonMobil Santoprene® 101-55W185 Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved