Samsung Cheil Industries Starex® VE-1801 HIPS, Unreinforced FR
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VE-1801 HIPS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
12 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.6 MPa | 3270 psi | 20 mm/min; ASTM D638 |
| Flexural Strength | 29.4 MPa | 4260 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.77 GPa | 256 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm |
1.84 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C @Thickness 6.40 mm |
160 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound
- Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
- Fiberfil® FPI-15 BK Nylon 6, 15% Glass Reinforced, post industrial
- Teknor Apex Monprene® MP 1627L3 Thermoplastic Elastomer
- Daikin DAI-EL G-575 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 70% Fluorine Content
- ChevronTexaco TEGRA® ISO 220 Synthetic Gear Lubricant
- Formosa Plastics Formolene® 6375N Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved