LG Chemical LUPOY GN2301F PC+GF30%, Halogen Free, Flame Retardant, Heat Resistance

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN2301F PC+GF30%, Halogen Free, Flame Retardant, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC+GF30%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0030 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 5.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 5.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 118 MPa

@Thickness 3.20 mm
 17100 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 2.0 %

@Thickness 3.20 mm
 2.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 177 MPa

@Thickness 3.20 mm
 25600 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 7.35 GPa

@Thickness 3.20 mm
 1070 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched >= 1.08 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 2.02 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 145 °C

@Thickness 6.40 mm
 >= 293 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 120 °C

@Thickness <=1.50 mm
 248 °F

@Thickness <=0.0591 in
120 °C

@Thickness <=3.00 mm
 248 °F

@Thickness <=0.118 in
UL RTI, Mechanical with Impact 90.0 °C

@Thickness >=1.50 mm
 194 °F

@Thickness >=0.0591 in
90.0 °C

@Thickness >=3.00 mm
 194 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 105 °C

@Thickness >=1.50 mm
 221 °F

@Thickness >=0.0591 in
105 °C

@Thickness >=3.00 mm
 221 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
5VB

@Thickness >=3.00 mm
 5VB

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 270 - 300 °C
518 - 572 °F
Injection Molding
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Injection Molding
Front Barrel Temperature 290 - 330 °C
554 - 626 °F
Injection Molding
Nozzle Temperature 290 - 330 °C
554 - 626 °F
Injection Molding
Melt Temperature 300 - 340 °C
572 - 644 °F
Injection Molding
Mold Temperature 90.0 - 120 °C
194 - 248 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding