PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | @ 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 6.8 % | 6.8 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.1 MPa | 13500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 701 ksi | ASTM D790 |
| Compressive Strength | 107 MPa | 15500 psi | ASTM D695 |
| Shear Strength | 66.9 MPa | 9700 psi | ASTM D732 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C @Thickness 3.18 mm |
415 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 3.18 mm |
405 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 559 °F | |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Glass Bead | |
| Glass Fiber Reinforcement | ||
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Nye Lubricants 757 (RL) Synthetic Oil
- RheTech Products T20P250-01UV 20% Talc Reinforced Polypropylene Copolymer, UV Stabilized, Black
- H.C. Starck Amperit® 518.074 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- DuPont™ Elvaloy® 741WR Ethylene/Vinyl Acetate/Carbon Monoxide (E/VA/CO) Copolymer
- ConocoPhillips Hydroclear® 40 Power-D E.O. 40
- Resirene Resirene® 7600 Super High Impact Polystyrene
- Axiall 4425 Flexible PVC
- SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific)
- SABIC Innovative Plastics LNP Verton UV007S PPA
Copyright © lookpolymers.com All Rights Reserved