PolyOne Edgetek® AS-20GF/000 HI UV NAT Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)&
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-20GF/000 HI UV NAT Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **)&.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedHigh ImpactUV StabilizedNaturalUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Compressive Strength | 93.1 MPa | 13500 psi | ASTM D695 |
| Shear Strength | 44.8 MPa | 6500 psi | ASTM D732 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.202 W/m-K | >= 1.40 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 215 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 227 - 260 °C | 440 - 500 °F | Molding |
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S3000-S2E Silver-Coated Solid Glass Spheres
- DuPont™ Clysar® AFG Polyolefin Shrink Packaging Film, Anti-fog, 60 Gauge (discontinued **)
- Solvay TECHNYL® A 230 PA66, DRY
- Shinil Chemical SHINSTAT ABS Electrostatic Control Polymer Injection Grade
- SABIC Innovative Plastics LNP STAT-LOY SLWM2105 PBT+PC (Asia Pacific)
- Dymax Sure Cure™ 984 Conformal Coating
- Braskem LH537 LLDPE Cast Film Extrusion Polyethylene
- Arlon 32580X030 0.030" (0.762 mm) Uncured Unsupported Silicone Rubber on a PET Carrier
- Eurofoam Porocell POR 300/100 Ethylene Octane Metallocene EPDM Foam
- Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, Dry As Molded
Copyright © lookpolymers.com All Rights Reserved