SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-loy* A3000 is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 29.0 MPa | 4210 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 21 % | 21 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.1 % | 3.1 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | >= 100 kJ/m² | >= 47.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 113 µm/m-°C @Temperature 23.0 - 60.0 °C |
62.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 124 µm/m-°C @Temperature 23.0 - 60.0 °C |
68.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs PT260 Na2PtBr6 Sodium hexabromoplatinate(IV)
- Niagara LaSalle 8620 Cold Finished Steel Bar
- Kraton® D1102 + LDPE blend (2/98)
- Teknor Apex Monprene® MP-1479 Thermoplastic Elastomer
- Formosa Plastics Formolon® 265 PVC
- Arlon 51588R015 0.015" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Ametek 17-4 P/M Process, Sintered at 2300°F (1260°C)
- A. Schulman ComAlloy Comtuf® 615 Nylon 6, Glass Reinforced, Impact Modified
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 1.0 PHR Sulfur
- ExxonMobil LL 1001.32 Cast Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved