PolyOne Bergamid™ XP6042701 Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ XP6042701 Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Speed: 50 to 80% Holding Time: 3 to 9 sec Injection Time: 1 to 3.5 sec Cycle Time: 18 to 60 secInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 165 MPa | 23900 psi | ASTM D638 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Charpy Impact, Notched | 90.0 J/cm² | 428 ft-lb/in² | J/m; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Nozzle Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Injection Pressure | 100 - 150 MPa | 14500 - 21800 psi | |
| Hold Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi | |
| Back Pressure | 0.300 - 0.500 MPa | 43.5 - 72.5 psi | |
| Screw Speed | 80 - 160 rpm | 80 - 160 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Carbon Fiber Reinforcement, 10% Filler by Weight | |
| Glass Fiber Reinforcement, 30% Filler by Weight | ||
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | Asia Pacific |
Users viewing this material also viewed the following:
- KB Alloys 50% Silicon Aluminum Alloy
- Borealis Daplen™ HJ060UB Polypropylene Compound for Direct Left Manufactured Applications
- Unipetrol Ethylhexanol
- Chi Mei Polylac® PA-747F ABS - Extrusion
- 3M AC-730 Class B-12 Aerospace Sealant
- ATI Allvac® Nickelvac® X- 751 UNS N07751 Nickel Superalloy
- CEN® Electronic Material HT Polyimide Film
- ArcelorMittal H 220 Solid solution steel, Cold rolled
- Polykemi AB POLYfill PPH T5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant
- Isoflon PCTFE Polychlorotrifluoroethylene
Copyright © lookpolymers.com All Rights Reserved