Arlon 55589G028 0.0295" (0.749 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 55589G028 0.0295" (0.749 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Interleave: PolyethyleneLayer 2: Uncured Silicone Rubber Layer 1: Cured Silicone Rubber Substrate: 162 Style FiberglassAppearance: Green silicone gum and rubber on fiberglass This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.34 g/cc	0.0484 lb/in³	Layer 1, Silicone Property; Arlon SQA-TMS-024
	1.56 g/cc	0.0564 lb/in³	Layer 2, Silicone Property; Arlon SQA-TMS-024
Thickness	76.2 microns	3.00 mil	Interleave
	102 microns	4.00 mil	Layer 1; Arlon SQA-TMS-003
	191 microns	7.50 mil	Layer 2; Arlon SQA-TMS-003
	457 microns	18.0 mil	Substrate; Arlon SQA-TMS-003
	749 microns	29.5 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	37	37	Layer 1, Silicone Property; ASTM D2240
	55	55	Layer 2, Silicone Property; ASTM D2240
Tensile Strength	3.65 MPa	530 psi	Layer 2, Silicone Property; ASTM D412
	6.55 MPa	950 psi	Layer 1, Silicone Property; ASTM D412
Elongation at Break	300 %	300 %	Layer 2, Silicone Property; ASTM D412
	620 %	620 %	Layer 1, Silicone Property; ASTM D412
Tear Strength	7.01 kN/m	40.0 pli	Layer 2, Silicone Property; ASTM D624
	26.3 kN/m	150 pli	Layer 1, Silicone Property; ASTM D624
Peel Strength	2.37 kN/m	13.5 pli	Bond Strength; ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
Flammability, UL94	HB @Temperature 200 °C	HB @Temperature 392 °F	per card E54153

Electrical Properties	Metric	English	Comments
Dielectric Strength	17.3 kV/mm	440 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 23.9 °C	6.00 Month @Temperature 75.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Green
Total Product Weight (oz/yd2)	33.3	Arlon SQA-TMS-025