PolyOne Bergamid™ A70 G5 T Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ A70 G5 T Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 3.40 J/cm² | 16.2 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.360 J/cm² | 1.71 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ALL; Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Glass Fiber Reinforcement, 5.0% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- MV Labs SM400 SmCl3·6H2O Samarium chloride hexahydrate
- SABIC HC100 Crystalline Polyethylene Terephthalate
- NOVA Chemicals Novapol® 5% LF-0718-A in PF-0118-B LDPE Film Resin
- PTS Trilac® FR3800-V Flame Retardant ABS Resin, RoHS Compliant
- Karina E 65/225 Compound PVC Crystal
- Kraton® D1102 + HDPE blend (20/80)
- A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer
- Teknor Apex Sinvicomp SIH 7005A Polyvinyl Chloride, Flexible
- Covestro Bayfol® AS-A 2-4 Polycarbonate + PBT
Copyright © lookpolymers.com All Rights Reserved