PlastiComp Complet® LCF40 - PA6 Nylon 6, 40% Long Carbon Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled
Manufacturer	PlastiComp
Trade Name	Complēt®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PlastiComp Complet® LCF40 - PA6 Nylon 6, 40% Long Carbon Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 40% carbon fiber reinforcementInformation provided by PlastiComp, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.33 g/cc	1.33 g/cc	ASTM D-792
Filler Content	40 %	40 %	Carbon Fiber

Mechanical Properties	Metric	English	Comments
Tensile Strength	290 MPa	42100 psi	ASTM D-638
Elongation at Break	1.0 %	1.0 %	ASTM D-638
Tensile Modulus	29.655 GPa	4301.1 ksi	ASTM D-638
Flexural Strength	428 MPa	62100 psi	ASTM D-790
Flexural Modulus	23.448 GPa	3400.9 ksi	ASTM D-790
Izod Impact, Notched	2.67 J/cm	5.00 ft-lb/in	ASTM D-256
Izod Impact, Unnotched	10.15 J/cm	19.02 ft-lb/in	ASTM D-4812

Processing Properties	Metric	English
Rear Barrel Temperature	260 - 277 °C	500 - 530 °F
Middle Barrel Temperature	266 - 282 °C	510 - 540 °F
Front Barrel Temperature	271 - 288 °C	520 - 550 °F
Nozzle Temperature	271 - 288 °C	520 - 550 °F
Melt Temperature	271 - 288 °C	520 - 550 °F
Mold Temperature	93.3 °C	200 °F
Injection Velocity	50.8 - 76.2 mm/sec	2.00 - 3.00 in/sec
Drying Temperature	85.0 °C @Time 14400 sec	185 °F @Time 4.00 hour
Moisture Content	<= 0.18 %	<= 0.18 %
Back Pressure	0.172 - 0.345 MPa	25.0 - 50.0 psi
Cushion	0.635 cm	0.250 in
Screw Speed	30 - 50 rpm	30 - 50 rpm

Descriptive Properties	Value	Comments
Injection Pressure	Medium to maximum