Kuraray Genestarâ„¢ GN2332 Nylon, 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ GN2332 Nylon, 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Flow V-0 Grade. Improves flow-ability in thin-walled parts. Used for components requiring high-flowability, such as 0.3 mm pitch connectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | |
| Water Absorption | 1.0 % | 1.0 % | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | |
| Melt Flow | 60 g/10 min @Load 2.16 kg, Temperature 320 °C |
60 g/10 min @Load 4.76 lb, Temperature 608 °F |
ASTM D1238 |
| Spiral Flow | 8.50 cm @Load 750 kg, Temperature 320 °C |
3.35 in @Load 1650 lb, Temperature 608 °F |
0.5mm diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 36.0 MPa | 5220 psi | Weld; ASTM D638 |
| 165 MPa | 23900 psi | ASTM D638 | |
| Elongation at Yield | 0.30 % | 0.30 % | Weld; ASTM D638 |
| 3.8 % | 3.8 % | ASTM D638 | |
| Flexural Strength | 215 MPa | 31200 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 306 °C | 583 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1.00e+10 Hz |
3.4 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dielectric Loss Index | 0.010 @Frequency 1.00e+10 Hz |
0.010 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | ASTM UL746A |
Users viewing this material also viewed the following:
- LG Chemical SEETEC BF410 LDPE
- Iran Petrochemical (PCC) TPC - 526 WP Expandable Polystyrene
- SYNTHOS Krasten® 137 General Purpose Polystyrene
- SABIC Innovative Plastics LNP LUBRILOY D2000 PC
- Techmer ES Plastiblend® PA6/6,6 IM 5050 BK Nylon 6/66
- Westlake EB502 12.5% EVA Copolymer
- 3M 433L Premium Performance Aluminum Foil Tape
- BASF Ultramid® A4H BK 00464 PA66 (Dry)
- Parker Chomerics CHO-BOND 1035 Electrically Conductive Sealant
- Polyram PlusTek RA321G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved