Plastcom SLOVAMID® 6/66 FRC 3 TS PA6/66 flame retarded, heat stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6/66
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID® 6/66 FRC 3 TS PA6/66 flame retarded, heat stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6 + PA 66 alloy for injection molding, reinforced with 30 % glass fiber, flame retarded with non halogen flame retardant, heat stabilized. Main features: flammability in accordance with UL 94 5 at 0,8 mm, glow wire at 960°C. Application for the electrical industry: protectors, coil forms, covers, terminals. Delivered in natural and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
STN EN ISO 1183-1
Filler Content 30 %
30 %
Glass Fiber
Linear Mold Shrinkage 0.0075 cm/cm
0.0075 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0087 cm/cm
0.0087 in/in
STN EN ISO 294-4
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
STN EN ISO 527-2
Elongation at Break 6.0 %
6.0 %
STN EN ISO 527-2
Tensile Modulus 3.65 GPa
529 ksi
STN EN ISO 527-2
Flexural Strength 125 MPa
18100 psi
STN EN ISO 178
Flexural Modulus 3.30 GPa
479 ksi
STN EN ISO 178
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -20.0 °C
38.1 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
8.50 J/cm²

@Temperature 23.0 °C
40.4 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 215 °C
419 °F
STN EN ISO 306
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Glow Wire Test 960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
STN EN 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
STN 34 6460
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
STN 34 6460
Dielectric Strength 25.0 kV/mm
635 kV/in
STN EN 60243-2
Comparative Tracking Index 600 V
600 V
STN EN 60112
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi