- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of this alloy.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.44 g/cc | 0.305 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 972 MPa | 141000 psi | |
| Tensile Strength, Yield | 529 MPa @Strain 0.200 % |
76700 psi @Strain 0.200 % |
|
| Elongation at Break | 42 % | 42 % | |
| Modulus of Elasticity | 208 GPa | 30200 ksi | |
| Poissons Ratio | 0.28 | 0.28 | |
| Shear Modulus | 81.4 GPa | 11800 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean | |
| Specific Heat Capacity | 0.410 J/g-°C | 0.0980 BTU/lb-°F | |
| Thermal Conductivity | 9.70 W/m-K | 67.3 BTU-in/hr-ft²-°F | |
| Melting Point | 1290 - 1350 °C | 2350 - 2460 °F | |
| Solidus | 1290 °C | 2350 °F | |
| Liquidus | 1350 °C | 2460 °F | |
| Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.40 % | <= 0.40 % | |
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 20 - 23 % | 20 - 23 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | <= 5.0 % | <= 5.0 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Molybdenum, Mo | 8.0 - 10 % | 8.0 - 10 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Niobium, Nb (Columbium, Cb) | 3.15 - 4.15 % | 3.15 - 4.15 % | Includes Ta |
| Nitrogen, N | <= 0.020 % | <= 0.020 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.020 % | <= 0.020 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Magnetic Permeability | 1.0006 | 1.0006 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- KYDEX® 321 Co-Extruded High Impact Fire Rated Sheet
- LyondellBasell Hifaxâ„¢ CB276 Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics NORYL SE1X PPE+PS (Asia Pacific)
- Styron Magnumâ„¢ 2620 ABS, Impact Grade
- SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific)
- Trelleborg Commercial Neoprene® C800 Chloroprene
- Eurostar Staramide BG6 PA6, 30% Glass Filled, Injection Molded
- Eurotec® Tecotek® PC40 GR30 NL PC, 30% glass fiber reinforced, natural
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 482°C Temper
Copyright © lookpolymers.com All Rights Reserved