PTS Tristar® PC-10R-CL02(V38) 38 MFI Polycarbonate with Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-10R-CL02(V38) 38 MFI Polycarbonate with Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | 24 hrs; ASTM D570 |
| Melt Flow | 38 g/10 min @Load 1.20 kg, Temperature 300 °C |
38 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 64.8 MPa @Thickness 3.17 mm |
9400 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 110 % @Thickness 3.17 mm |
110 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 82.7 MPa @Thickness 3.17 mm |
12000 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.34 GPa @Thickness 3.17 mm |
340 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
18.3 µin/in-°F @Temperature -40.0 - 203 °F |
|
| CTE, linear, Transverse to Flow | 33.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
18.3 µin/in-°F @Temperature -40.0 - 203 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ASTM D648 |
| UL RTI, Electrical | 125 °C | 257 °F | |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | PLC 6 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC 2 |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 1.50 mm |
15 - 30 sec @Thickness 0.0591 in |
PLC 3 |
| 30 - 60 sec @Thickness 3.00 mm |
30 - 60 sec @Thickness 0.118 in |
PLC 2 | |
| High Amp Arc Ignition, HAI | 60 - 120 arcs @Thickness 3.00 mm |
60 - 120 arcs @Thickness 0.118 in |
PLC 1 |
| >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
PLC 0 | |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC 3 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion L0678 Natural Polyvinyl Chloride, Rigid (PVC, Rigid)
- Permabond HM128 Anaerobic Threadlocker
- ExxonMobil Escorene® LD-102 LDPE Drawdown Resin, 1.25 mil Film (discontinued **)
- DSM Akulon® K230-HXG6 Nylon 6-30% Glass Reinforced (European Grade) (Dry) (discontinued **)
- Karina 651-48/1-BY-IS Black PVC Compound
- Techmer ES Luriblend® PA6 ML3 BK Nylon 6
- Goodfellow Carbon/Vinyl Ester Rod
- Universal Wire Works 13-8Mo (AMS 5840) Filler Metal
- ATI Allvac® 6-2-4-2-Si UNS R54620 modified Titanium Alloy
- Unitika P-3001 Engineering Plastic
Copyright © lookpolymers.com All Rights Reserved