DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Impact Modified
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Toughened Polyamide 612 Developed for ExtrusionInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 0.820 g/cc
0.0296 lb/in³
1.00 g/cc
0.0361 lb/in³
DAM; ISO 1183
Viscosity 74000 cP

@Shear Rate 5000 1/s,
Temperature 270 °C
 74000 cP

@Shear Rate 5000 1/s,
Temperature 518 °F
 ISO 11403-1 -2
88000 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 88000 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
109890 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 109890 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
280000 cP

@Shear Rate 500 1/s,
Temperature 270 °C
 280000 cP

@Shear Rate 500 1/s,
Temperature 518 °F
 ISO 11403-1 -2
349000 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 349000 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
425090 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 425090 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.028 cm/cm
0.028 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Stress 0.850 MPa

@Strain 0.110 %,
Temperature 40.0 °C
 123 psi

@Strain 0.110 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
1.13 MPa

@Strain 0.0800 %,
Temperature 23.0 °C
 164 psi

@Strain 0.0800 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
1.21 MPa

@Strain 0.0800 %,
Temperature 0.000 °C
 175 psi

@Strain 0.0800 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
1.33 MPa

@Strain 0.0600 %,
Temperature -20.0 °C
 193 psi

@Strain 0.0600 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
2.37 MPa

@Strain 0.920 %,
Temperature 90.0 °C
 344 psi

@Strain 0.920 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
2.82 MPa

@Strain 3.27 %,
Temperature 150 °C
 409 psi

@Strain 3.27 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
2.83 MPa

@Strain 0.440 %,
Temperature 40.0 °C
 410 psi

@Strain 0.440 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
3.18 MPa

@Strain 4.50 %,
Temperature 150 °C
 461 psi

@Strain 4.50 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
3.44 MPa

@Strain 0.230 %,
Temperature 0.000 °C
 499 psi

@Strain 0.230 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
4.05 MPa

@Strain 0.400 %,
Temperature 23.0 °C
 587 psi

@Strain 0.400 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
4.23 MPa

@Strain 0.240 %,
Temperature -20.0 °C
 614 psi

@Strain 0.240 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
5.32 MPa

@Strain 0.230 %,
Temperature -40.0 °C
 772 psi

@Strain 0.230 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
5.51 MPa

@Strain 2.96 %,
Temperature 90.0 °C
 799 psi

@Strain 2.96 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
7.10 MPa

@Strain 48.0 %,
Temperature 150 °C
 1030 psi

@Strain 48.0 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
13.6 MPa

@Strain 48.45 %,
Temperature 90.0 °C
 1970 psi

@Strain 48.45 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
14.12 MPa

@Strain 39.22 %,
Temperature 90.0 °C
 2048 psi

@Strain 39.22 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
14.93 MPa

@Strain 0.710 %,
Temperature -40.0 °C
 2165 psi

@Strain 0.710 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
17.6 MPa

@Strain 1.36 %,
Temperature 0.000 °C
 2550 psi

@Strain 1.36 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
20.87 MPa

@Strain 11.52 %,
Temperature 40.0 °C
 3027 psi

@Strain 11.52 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
21.0 MPa

@Strain 5.34 %,
Temperature 40.0 °C
 3050 psi

@Strain 5.34 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
21.54 MPa

@Strain 2.11 %,
Temperature 23.0 °C
 3124 psi

@Strain 2.11 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
22.66 MPa

@Strain 24.42 %,
Temperature 40.0 °C
 3287 psi

@Strain 24.42 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
24.84 MPa

@Strain 17.81 %,
Temperature 40.0 °C
 3603 psi

@Strain 17.81 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
25.45 MPa

@Strain 31.26 %,
Temperature 40.0 °C
 3691 psi

@Strain 31.26 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
27.84 MPa

@Strain 9.53 %,
Temperature 23.0 °C
 4038 psi

@Strain 9.53 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
29.26 MPa

@Strain 20.72 %,
Temperature 23.0 °C
 4244 psi

@Strain 20.72 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
32.3 MPa

@Strain 12.4 %,
Temperature 23.0 °C
 4680 psi

@Strain 12.4 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
39.26 MPa

@Strain 8.21 %,
Temperature 0.000 °C
 5694 psi

@Strain 8.21 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
40.8 MPa

@Strain 10.85 %,
Temperature 0.000 °C
 5920 psi

@Strain 10.85 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
47.34 MPa

@Strain 3.08 %,
Temperature -40.0 °C
 6866 psi

@Strain 3.08 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
47.91 MPa

@Strain 8.21 %,
Temperature -20.0 °C
 6949 psi

@Strain 8.21 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
53.18 MPa

@Strain 4.52 %,
Temperature -40.0 °C
 7713 psi

@Strain 4.52 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
60.95 MPa

@Strain 8.91 %,
Temperature -40.0 °C
 8840 psi

@Strain 8.91 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
62.14 MPa

@Strain 7.35 %,
Temperature -40.0 °C
 9013 psi

@Strain 7.35 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Tensile Strength, Yield 28.0 MPa
4060 psi
50%RH; ISO 527-1/-2
30.0 MPa
4350 psi
DAM; ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
DAM; Nominal; ISO 527-1/-2
>= 50 %
>= 50 %
50%RH; Nominal; ISO 527-1/-2
Elongation at Yield 20 %
20 %
DAM; ISO 527-1/-2
30 %
30 %
50%RH; ISO 527-1/-2
Tensile Modulus 0.720 GPa
104 ksi
50%RH; ISO 527-1/-2
1.08 GPa
157 ksi
DAM; ISO 527-1/-2
0.110 GPa

@Temperature 120 °C
 16.0 ksi

@Temperature 248 °F
 50%RH; ISO 11403-1 -2
0.130 GPa

@Temperature 120 °C
 18.9 ksi

@Temperature 248 °F
 DAM; ISO 11403-1 -2
0.455 GPa

@Temperature 40.0 °C
 66.0 ksi

@Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.680 GPa

@Temperature 40.0 °C
 98.6 ksi

@Temperature 104 °F
 DAM; ISO 11403-1 -2
2.119 GPa

@Temperature -40.0 °C
 307.3 ksi

@Temperature -40.0 °F
 DAM; ISO 11403-1 -2
2.196 GPa

@Temperature -40.0 °C
 318.5 ksi

@Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
Secant Modulus 0.0786 GPa

@Strain 29.03 %,
Temperature 40.0 °C
 11.4 ksi

@Strain 29.03 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.114 GPa

@Strain 22.16 %,
Temperature 40.0 °C
 16.5 ksi

@Strain 22.16 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.181 GPa

@Strain 11.52 %,
Temperature 40.0 °C
 26.3 ksi

@Strain 11.52 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
0.29213 GPa

@Strain 9.53 %,
Temperature 23.0 °C
 42.371 ksi

@Strain 9.53 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
0.393 GPa

@Strain 5.34 %,
Temperature 40.0 °C
 57.0 ksi

@Strain 5.34 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
0.402 GPa

@Strain 12.06 %,
Temperature -20.0 °C
 58.3 ksi

@Strain 12.06 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
0.478 GPa

@Strain 8.21 %,
Temperature 0.000 °C
 69.4 ksi

@Strain 8.21 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2