Overview of materials for Polyethylene Terephthalate (PET), Glass/Mineral Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass/Mineral Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyethylene Terephthalate (PET), Glass/Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.42 - 1.83 g/cc
0.0514 - 0.0661 lb/in³
Average value: 1.61 g/cc Grade Count:48
Water Absorption 0.0300 - 0.750 %
0.0300 - 0.750 %
Average value: 0.101 % Grade Count:13
Moisture Absorption at Equilibrium 0.0500 - 0.240 %
0.0500 - 0.240 %
Average value: 0.148 % Grade Count:9
Linear Mold Shrinkage 0.00100 - 0.0110 cm/cm
0.00100 - 0.0110 in/in
Average value: 0.00341 cm/cm Grade Count:33
Linear Mold Shrinkage, Transverse 0.00530 - 0.0100 cm/cm
0.00530 - 0.0100 in/in
Average value: 0.00804 cm/cm Grade Count:19
Ash 25.0 - 35.0 %
25.0 - 35.0 %
Average value: 31.7 % Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell M 87.0 - 115
87.0 - 115
Average value: 97.7 Grade Count:3
Hardness, Rockwell R 109 - 120
109 - 120
Average value: 116 Grade Count:12
Tensile Strength, Ultimate 90.0 - 195 MPa
13100 - 28300 psi
Average value: 117 MPa Grade Count:44
45.0 - 145 MPa

@Temperature -40.0 - 120 °C
6530 - 21000 psi

@Temperature -40.0 - 248 °F
Average value: 83.3 MPa Grade Count:1
Tensile Strength, Yield 91.0 - 145 MPa
13200 - 21000 psi
Average value: 114 MPa Grade Count:4
Elongation at Break 1.00 - 7.00 %
1.00 - 7.00 %
Average value: 2.34 % Grade Count:38
1.60 - 8.10 %

@Temperature -40.0 - 120 °C
1.60 - 8.10 %

@Temperature -40.0 - 248 °F
Average value: 5.33 % Grade Count:1
Modulus of Elasticity 11.0 - 13.8 GPa
1600 - 2000 ksi
Average value: 12.0 GPa Grade Count:9
2.59 - 12.27 GPa

@Temperature -40.0 - 120 °C
376 - 1780 ksi

@Temperature -40.0 - 248 °F
Average value: 6.33 GPa Grade Count:1
Flexural Yield Strength 130 - 265 MPa
18900 - 38400 psi
Average value: 182 MPa Grade Count:42
Flexural Modulus 6.30 - 15.5 GPa
914 - 2250 ksi
Average value: 9.65 GPa Grade Count:44
Compressive Yield Strength 126 - 151 MPa
18300 - 21900 psi
Average value: 141 MPa Grade Count:3
Izod Impact, Notched 0.430 - 0.910 J/cm
0.806 - 1.70 ft-lb/in
Average value: 0.649 J/cm Grade Count:26
Izod Impact, Unnotched 4.27 - 5.34 J/cm
8.00 - 10.0 ft-lb/in
Average value: 4.85 J/cm Grade Count:6
Izod Impact, Notched (ISO) 6.00 - 59.0 kJ/m²
2.86 - 28.1 ft-lb/in²
Average value: 14.0 kJ/m² Grade Count:7
5.00 - 5.00 kJ/m²

@Temperature -30.0 - -30.0 °C
2.38 - 2.38 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.00 kJ/m² Grade Count:1
Charpy Impact Unnotched 2.60 - 3.50 J/cm²
12.4 - 16.7 ft-lb/in²
Average value: 3.03 J/cm² Grade Count:3
2.20 - 3.50 J/cm²

@Temperature -40.0 - -30.0 °C
10.5 - 16.7 ft-lb/in²

@Temperature -40.0 - -22.0 °F
Average value: 2.85 J/cm² Grade Count:2
Charpy Impact, Notched 0.320 - 0.860 J/cm²
1.52 - 4.09 ft-lb/in²
Average value: 0.674 J/cm² Grade Count:19
0.530 - 0.600 J/cm²

@Temperature -40.0 - -30.0 °C
2.52 - 2.86 ft-lb/in²

@Temperature -40.0 - -22.0 °F
Average value: 0.560 J/cm² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 15.0 - 59.4 µm/m-°C
8.33 - 33.0 µin/in-°F
Average value: 24.1 µm/m-°C Grade Count:14
0.140 - 6.00 µm/m-°C

@Temperature 55.0 - 160 °C
0.0778 - 3.33 µin/in-°F

@Temperature 131 - 320 °F
Average value: 3.07 µm/m-°C Grade Count:2
CTE, linear, Transverse to Flow 0.610 - 87.0 µm/m-°C
0.339 - 48.3 µin/in-°F
Average value: 55.9 µm/m-°C Grade Count:8
1.10 - 84.0 µm/m-°C

@Temperature 55.0 - 160 °C
0.611 - 46.7 µin/in-°F

@Temperature 131 - 320 °F
Average value: 42.5 µm/m-°C Grade Count:2
Melting Point 232 - 268 °C
450 - 514 °F
Average value: 251 °C Grade Count:20
Maximum Service Temperature, Air 75.0 - 140 °C
167 - 284 °F
Average value: 115 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 94.0 - 243 °C
201 - 470 °F
Average value: 223 °C Grade Count:12
Deflection Temperature at 1.8 MPa (264 psi) 79.0 - 242 °C
174 - 468 °F
Average value: 212 °C Grade Count:48
Vicat Softening Point 225 °C
437 °F
Average value: 225 °C Grade Count:4
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:31
Electrical Properties Metric English Comments
Electrical Resistivity 5.00e+14 - 1.00e+17 ohm-cm
5.00e+14 - 1.00e+17 ohm-cm
Average value: 2.43e+16 ohm-cm Grade Count:24
Surface Resistance 1.00e+13 - 1.00e+17 ohm
1.00e+13 - 1.00e+17 ohm
Average value: 5.27e+16 ohm Grade Count:19
Dielectric Constant 3.50 - 3.80
3.50 - 3.80
Average value: 3.72 Grade Count:8
Dielectric Strength 16.2 - 38.0 kV/mm
411 - 965 kV/in
Average value: 21.8 kV/mm Grade Count:25
Dissipation Factor 0.00500 - 0.0160
0.00500 - 0.0160
Average value: 0.0102 Grade Count:7
Arc Resistance 75.0 - 125 sec
75.0 - 125 sec
Average value: 94.8 sec Grade Count:4
Comparative Tracking Index 175 - 250 V
175 - 250 V
Average value: 219 V Grade Count:16
Processing Properties Metric English Comments
Processing Temperature 110 - 300 °C
230 - 572 °F
Average value: 246 °C Grade Count:4
Nozzle Temperature 270 - 300 °C
518 - 572 °F
Average value: 286 °C Grade Count:7
Melt Temperature 20.0 - 304 °C
68.0 - 579 °F
Average value: 274 °C Grade Count:22
Mold Temperature 65.0 - 140 °C
149 - 284 °F
Average value: 108 °C Grade Count:22
Drying Temperature 120 - 140 °C
248 - 284 °F
Average value: 125 °C Grade Count:8
Moisture Content 0.0100 - 0.0800 %
0.0100 - 0.0800 %
Average value: 0.0243 % Grade Count:7
Injection Pressure 50.0 - 120 MPa
7250 - 17400 psi
Average value: 72.1 MPa Grade Count:6