- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 6
- Nylon 6, 50% Glass Fiber Filled
- Solvay TECHNYLSTARâ„¢ AFX 218S V50 PA6, 50% glass filled, DRY
Solvay TECHNYLSTARâ„¢ AFX 218S V50 PA6, 50% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYLSTAR™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYLSTARâ„¢ AFX 218S V50 PA6, 50% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High stiffness materials TECHNYLSTAR Polyamide 66, reinforced with 50% of glass fiber, heat stabilized for injection molding. Characterized by a high fluidity of the melt. Available in: Asia Pacific Product Applications: TECHNYLSTAR AFX 218S V50 BLACK 31N is used in automotive industry and industrial parts, demanding high mechanical strength, stiffness, thermal stability and excellent surface aspect, by a very easy flow and low injection molding pressure. This grade is widely used for automotive parts such as structural parts, brackets and pulleys. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183/A |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0034 cm/cm | 0.0034 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0042 cm/cm | 0.0042 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D786 |
| Tensile Strength, Yield | 230 MPa | 33400 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 355 MPa | 51500 psi | ASTM D790 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ASTM D790 |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 256 °C | 493 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- LG Chemical RS657 ABS, Chemical Resistance to Cyclopentane
- Shinil Chemical SHINSTRA PP (SM400) Structural Polymer Household
- Suzhou Hipro Polymers Hiprolon® 70 NN Nylon 610, dry
- Plenco 1530 Polyester, Briquette, Injection Molded
- Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric
- DAK Americas Laser+® W 4000 K42A PET
- DuPont Performance Polymers Zytel® RS LC2800 NC010 Nylon (Unverified Data**)
- Buckeye Polymers BP RPP 2011 C Polypropylene, 20% Mineral Filled
- Axiall 2502 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved