Overview of materials for Nylon 6, Cast

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 6, Cast.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.679 - 1.17 g/cc
0.0245 - 0.0423 lb/in³
Average value: 1.14 g/cc Grade Count:63
Water Absorption 0.300 - 7.00 %
0.300 - 7.00 %
Average value: 1.37 % Grade Count:28
Moisture Absorption at Equilibrium 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 2.05 % Grade Count:33
Water Absorption at Saturation 2.50 - 7.00 %
2.50 - 7.00 %
Average value: 5.75 % Grade Count:48
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80.0 - 88.0
80.0 - 88.0
Average value: 84.9 Grade Count:16
Hardness, Rockwell R 100 - 120
100 - 120
Average value: 113 Grade Count:22
Hardness, Shore D 74.0 - 85.0
74.0 - 85.0
Average value: 80.2 Grade Count:28
Ball Indentation Hardness 70.0 - 175 MPa
10200 - 25400 psi
Average value: 140 MPa Grade Count:35
Tensile Strength, Ultimate 43.1 - 90.0 MPa
6250 - 13100 psi
Average value: 75.5 MPa Grade Count:38
Tensile Strength, Yield 40.0 - 100 MPa
5800 - 14500 psi
Average value: 70.8 MPa Grade Count:27
Elongation at Break 2.30 - 120 %
2.30 - 120 %
Average value: 36.4 % Grade Count:49
Elongation at Yield 5.00 %
5.00 %
Average value: 5.00 % Grade Count:5
Creep Strength 6.00 - 24.0 MPa
870 - 3480 psi
Average value: 15.6 MPa Grade Count:15
Modulus of Elasticity 1.30 - 4.20 GPa
189 - 609 ksi
Average value: 2.96 GPa Grade Count:64
0.400 - 0.800 GPa

@Temperature 100 - 100 °C
58.0 - 116 ksi

@Temperature 212 - 212 °F
Average value: 0.600 GPa Grade Count:2
Flexural Yield Strength 20.0 - 150 MPa
2900 - 21800 psi
Average value: 96.3 MPa Grade Count:48
Flexural Modulus 1.30 - 3.70 GPa
189 - 537 ksi
Average value: 2.81 GPa Grade Count:45
Compressive Yield Strength 6.00 - 162 MPa
870 - 23500 psi
Average value: 66.0 MPa Grade Count:42
Compressive Modulus 1.52 - 2.76 GPa
220 - 400 ksi
Average value: 2.28 GPa Grade Count:20
Shear Strength 44.8 - 75.8 MPa
6500 - 11000 psi
Average value: 66.3 MPa Grade Count:15
Izod Impact, Notched 0.160 - 0.961 J/cm
0.300 - 1.80 ft-lb/in
Average value: 0.484 J/cm Grade Count:22
Izod Impact, Notched (ISO) 2.50 - 100000 kJ/m²
1.19 - 47600 ft-lb/in²
Average value: 11.1 kJ/m² Grade Count:19
Charpy Impact Unnotched 5.00 J/cm² - NB
23.8 ft-lb/in² - NB
Average value: 5.63 J/cm² Grade Count:18
Charpy Impact, Notched 0.300 - 10.0 J/cm²
1.43 - 47.6 ft-lb/in²
Average value: 1.24 J/cm² Grade Count:20
Tensile Impact Strength 72.0 kJ/m²
34.3 ft-lb/in²
Average value: 72.0 kJ/m² Grade Count:3
Coefficient of Friction 0.0400 - 0.600
0.0400 - 0.600
Average value: 0.233 Grade Count:49
Coefficient of Friction, Static 0.200 - 0.350
0.200 - 0.350
Average value: 0.240 Grade Count:5
Tear Strength Test 0.150 - 1.80
0.150 - 1.80
Average value: 0.375 Grade Count:14
K Factor (Wear Factor) 4.00e-11 - 1.00e-10
4.00e-11 - 1.00e-10
Average value: 7.67e-11 Grade Count:12
K (wear) Factor 8.06 - 500 x 10-8 mm³/N-M
4.00 - 248 x 10-10 in³-min/ft-lb-hr
Average value: 203 x 10<sup>-8</sup> mm³/N-M Grade Count:12
Limiting Pressure Velocity 0.0800 - 1.33 MPa-m/sec
2280 - 38000 psi-ft/min
Average value: 0.412 MPa-m/sec Grade Count:12
Thermal Properties Metric English Comments
CTE, linear 63.0 - 180 µm/m-°C
35.0 - 100 µin/in-°F
Average value: 81.9 µm/m-°C Grade Count:62
Specific Heat Capacity 1.67 - 1.67 J/g-°C
0.399 - 0.400 BTU/lb-°F
Average value: 1.67 J/g-°C Grade Count:17
Thermal Conductivity 0.0259 - 0.342 W/m-K
0.180 - 2.37 BTU-in/hr-ft²-°F
Average value: 0.260 W/m-K Grade Count:41
Melting Point 190 - 238 °C
374 - 460 °F
Average value: 219 °C Grade Count:60
Maximum Service Temperature, Air 60.0 - 180 °C
140 - 356 °F
Average value: 131 °C Grade Count:61
Deflection Temperature at 0.46 MPa (66 psi) 160 - 221 °C
320 - 430 °F
Average value: 203 °C Grade Count:30
Deflection Temperature at 1.8 MPa (264 psi) 75.0 - 204 °C
167 - 399 °F
Average value: 117 °C Grade Count:45
Minimum Service Temperature, Air -100 - -20.0 °C
-148 - -4.00 °F
Average value: -45.1 °C Grade Count:34
Glass Transition Temp, Tg 5.00 - 50.0 °C
41.0 - 122 °F
Average value: 39.2 °C Grade Count:5
Flammability, UL94 HB - V-2
HB - V-2
Grade Count:32
Oxygen Index 25.0 %
25.0 %
Average value: 25.0 % Grade Count:6
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 1.00e+15 ohm-cm
1.00e+12 - 1.00e+15 ohm-cm
Average value: 3.61e+14 ohm-cm Grade Count:39
Surface Resistance 1.00e+10 - 1.00e+13 ohm
1.00e+10 - 1.00e+13 ohm
Average value: 4.31e+12 ohm Grade Count:35
Dielectric Constant 3.10 - 12.0
3.10 - 12.0
Average value: 3.94 Grade Count:51
Dielectric Strength 15.0 - 100 kV/mm
381 - 2540 kV/in
Average value: 27.8 kV/mm Grade Count:48
Dissipation Factor 0.00200 - 0.150
0.00200 - 0.150
Average value: 0.0239 Grade Count:16
Dielectric Loss Index 0.0120 - 0.140
0.0120 - 0.140
Average value: 0.0318 Grade Count:17
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:12