DuPont Performance Polymers Hytrel® HTR8163HVBK Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8163HVBK Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
65 Shore D Polyester Elastomer with Heat Ageing Protection Developed for ExtrusionInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
1.23 g/cc
0.0444 lb/in³
ISO 1183
Viscosity 91910 cP

@Shear Rate 5000 1/s,
Temperature 245 °C
91910 cP

@Shear Rate 5000 1/s,
Temperature 473 °F
ISO 11403-1 -2
99440 cP

@Shear Rate 5000 1/s,
Temperature 235 °C
99440 cP

@Shear Rate 5000 1/s,
Temperature 455 °F
ISO 11403-1 -2
108100 cP

@Shear Rate 5000 1/s,
Temperature 225 °C
108100 cP

@Shear Rate 5000 1/s,
Temperature 437 °F
ISO 11403-1 -2
387800 cP

@Shear Rate 500 1/s,
Temperature 245 °C
387800 cP

@Shear Rate 500 1/s,
Temperature 473 °F
ISO 11403-1 -2
431600 cP

@Shear Rate 500 1/s,
Temperature 235 °C
431600 cP

@Shear Rate 500 1/s,
Temperature 455 °F
ISO 11403-1 -2
480900 cP

@Shear Rate 500 1/s,
Temperature 225 °C
480900 cP

@Shear Rate 500 1/s,
Temperature 437 °F
ISO 11403-1 -2
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
cm³/10min; ISO 1133
5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
15s; ISO 868
<= 65
<= 65
ISO 868
Tensile Strength at Break 44.0 MPa
6380 psi
ISO 527-1/-2
Tensile Stress 12.0 MPa

@Strain 5.00 %
1740 psi

@Strain 5.00 %
ISO 527-1/-2
17.8 MPa

@Strain 10.0 %
2580 psi

@Strain 10.0 %
ISO 527-1/-2
20.0 MPa

@Strain 50.0 %
2900 psi

@Strain 50.0 %
ISO 527-1/-2
23.0 MPa

@Strain 100 %
3340 psi

@Strain 100 %
ISO 527-1/-2
32.0 MPa

@Strain 300 %
4640 psi

@Strain 300 %
ISO 527-1/-2
0.230 MPa

@Strain 0.0500 %,
Temperature 200 °C
33.4 psi

@Strain 0.0500 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
0.250 MPa

@Strain 0.180 %,
Temperature 200 °C
36.3 psi

@Strain 0.180 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
0.350 MPa

@Strain 0.0500 %,
Temperature 180 °C
50.8 psi

@Strain 0.0500 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
0.360 MPa

@Strain 0.0400 %,
Temperature 150 °C
52.2 psi

@Strain 0.0400 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
0.380 MPa

@Strain 0.0400 %,
Temperature 120 °C
55.1 psi

@Strain 0.0400 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
0.410 MPa

@Strain 0.0400 %,
Temperature 90.0 °C
59.5 psi

@Strain 0.0400 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
0.420 MPa

@Strain 0.210 %,
Temperature 180 °C
60.9 psi

@Strain 0.210 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
0.430 MPa

@Strain 0.0400 %,
Temperature 60.0 °C
62.4 psi

@Strain 0.0400 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
0.450 MPa

@Strain 0.0200 %,
Temperature 0.000 °C
65.3 psi

@Strain 0.0200 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
0.480 MPa

@Strain 0.0200 %,
Temperature -20.0 °C
69.6 psi

@Strain 0.0200 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
0.490 MPa

@Strain 0.220 %,
Temperature 150 °C
71.1 psi

@Strain 0.220 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
0.540 MPa

@Strain 0.170 %,
Temperature 120 °C
78.3 psi

@Strain 0.170 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
0.580 MPa

@Strain 0.0600 %,
Temperature 23.0 °C
84.1 psi

@Strain 0.0600 %,
Temperature 73.4 °F
TPE; ISO 11403-1 -2
0.640 MPa

@Strain 0.200 %,
Temperature 90.0 °C
92.8 psi

@Strain 0.200 %,
Temperature 194 °F
TPE; ISO 11403-1 -2
0.690 MPa

@Strain 3.32 %,
Temperature 200 °C
100 psi

@Strain 3.32 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
0.710 MPa

@Strain 0.190 %,
Temperature 60.0 °C
103 psi

@Strain 0.190 %,
Temperature 140 °F
TPE; ISO 11403-1 -2
0.970 MPa

@Strain 0.120 %,
Temperature 0.000 °C
141 psi

@Strain 0.120 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
1.22 MPa

@Strain 0.250 %,
Temperature 23.0 °C
177 psi

@Strain 0.250 %,
Temperature 73.4 °F
TPE; ISO 11403-1 -2
1.23 MPa

@Strain 10.41 %,
Temperature 200 °C
178 psi

@Strain 10.41 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
1.27 MPa

@Strain 0.100 %,
Temperature -20.0 °C
184 psi

@Strain 0.100 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
1.46 MPa

@Strain 0.210 %,
Temperature 0.000 °C
212 psi

@Strain 0.210 %,
Temperature 32.0 °F
TPE; ISO 11403-1 -2
1.46 MPa

@Strain 18.09 %,
Temperature 200 °C
212 psi

@Strain 18.09 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
1.66 MPa

@Strain 34.33 %,
Temperature 200 °C
241 psi

@Strain 34.33 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
2.07 MPa

@Strain 82.96 %,
Temperature 200 °C
300 psi

@Strain 82.96 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
2.07 MPa

@Strain 0.160 %,
Temperature -20.0 °C
300 psi

@Strain 0.160 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
2.15 MPa

@Strain 92.53 %,
Temperature 200 °C
312 psi

@Strain 92.53 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
2.27 MPa

@Strain 106.46 %,
Temperature 200 °C
329 psi

@Strain 106.46 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
2.40 MPa

@Strain 124.88 %,
Temperature 200 °C
348 psi

@Strain 124.88 %,
Temperature 392 °F
TPE; ISO 11403-1 -2
2.80 MPa

@Strain 0.220 %,
Temperature -20.0 °C
406 psi

@Strain 0.220 %,
Temperature -4.00 °F
TPE; ISO 11403-1 -2
3.25 MPa

@Strain 0.140 %,
Temperature -40.0 °C
471 psi

@Strain 0.140 %,
Temperature -40.0 °F
TPE; ISO 11403-1 -2
3.52 MPa

@Strain 21.33 %,
Temperature 180 °C
511 psi

@Strain 21.33 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
3.98 MPa

@Strain 60.25 %,
Temperature 180 °C
577 psi

@Strain 60.25 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
4.40 MPa

@Strain 93.62 %,
Temperature 180 °C
638 psi

@Strain 93.62 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
4.98 MPa

@Strain 129.19 %,
Temperature 180 °C
722 psi

@Strain 129.19 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
5.60 MPa

@Strain 159.43 %,
Temperature 180 °C
812 psi

@Strain 159.43 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
6.28 MPa

@Strain 187.51 %,
Temperature 180 °C
911 psi

@Strain 187.51 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
6.54 MPa

@Strain 24.54 %,
Temperature 150 °C
949 psi

@Strain 24.54 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
6.84 MPa

@Strain 214.38 %,
Temperature 180 °C
992 psi

@Strain 214.38 %,
Temperature 356 °F
TPE; ISO 11403-1 -2
7.23 MPa

@Strain 65.52 %,
Temperature 150 °C
1050 psi

@Strain 65.52 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
7.80 MPa

@Strain 11.79 %,
Temperature 120 °C
1130 psi

@Strain 11.79 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
7.83 MPa

@Strain 103.46 %,
Temperature 150 °C
1140 psi

@Strain 103.46 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
8.67 MPa

@Strain 0.360 %,
Temperature -40.0 °C
1260 psi

@Strain 0.360 %,
Temperature -40.0 °F
TPE; ISO 11403-1 -2
8.80 MPa

@Strain 140.7 %,
Temperature 150 °C
1280 psi

@Strain 140.7 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
9.87 MPa

@Strain 171.75 %,
Temperature 150 °C
1430 psi

@Strain 171.75 %,
Temperature 302 °F
TPE; ISO 11403-1 -2
10.04 MPa

@Strain 49.19 %,
Temperature 120 °C
1456 psi

@Strain 49.19 %,
Temperature 248 °F
TPE; ISO 11403-1 -2
10.39 MPa

@Strain 318.1 %,
Temperature 180 °C
1507 psi

@Strain 318.1 %,
Temperature 356 °F
TPE; ISO 11403-1 -2