Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Heat Resistant, Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.19 g/cc
0.0415 - 0.0430 lb/in³
Average value: 1.18 g/cc Grade Count:17
Water Absorption 0.300 - 2.00 %
0.300 - 2.00 %
Average value: 0.490 % Grade Count:10
Water Absorption at Saturation 0.300 %
0.300 %
Average value: 0.300 % Grade Count:4
Linear Mold Shrinkage 0.00200 - 0.00700 cm/cm
0.00200 - 0.00700 in/in
Average value: 0.00423 cm/cm Grade Count:15
Melt Flow 0.900 - 19.0 g/10 min
0.900 - 19.0 g/10 min
Average value: 3.77 g/10 min Grade Count:17
Mechanical Properties Metric English Comments
Hardness, Rockwell M 44.0 - 105
44.0 - 105
Average value: 85.7 Grade Count:14
Tensile Strength, Ultimate 44.1 - 80.0 MPa
6400 - 11600 psi
Average value: 67.0 MPa Grade Count:14
Tensile Strength, Yield 71.7 - 76.0 MPa
10400 - 11000 psi
Average value: 74.4 MPa Grade Count:3
Elongation at Break 3.00 - 30.0 %
3.00 - 30.0 %
Average value: 11.8 % Grade Count:15
Elongation at Yield 4.00 - 13.0 %
4.00 - 13.0 %
Average value: 6.14 % Grade Count:7
Modulus of Elasticity 1.72 - 3.60 GPa
250 - 522 ksi
Average value: 2.86 GPa Grade Count:14
Flexural Yield Strength 68.9 - 133 MPa
10000 - 19300 psi
Average value: 103 MPa Grade Count:15
Flexural Modulus 1.79 - 3.43 GPa
260 - 498 ksi
Average value: 2.87 GPa Grade Count:14
Izod Impact, Notched 0.157 - 0.534 J/cm
0.294 - 1.00 ft-lb/in
Average value: 0.280 J/cm Grade Count:13
0.240255 - 0.32034 J/cm

@Temperature 0.000 - 0.000 °C
0.450096 - 0.60013 ft-lb/in

@Temperature 32.0 - 32.0 °F
Average value: 0.274 J/cm Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 59.9 - 75.0 µm/m-°C
33.3 - 41.7 µin/in-°F
Average value: 65.0 µm/m-°C Grade Count:3
72.0 - 90.0 µm/m-°C

@Temperature 0.000 - 156 °C
40.0 - 50.0 µin/in-°F

@Temperature 32.0 - 312 °F
Average value: 76.5 µm/m-°C Grade Count:4
Thermal Conductivity 0.187 - 0.210 W/m-K
1.30 - 1.46 BTU-in/hr-ft²-°F
Average value: 0.193 W/m-K Grade Count:8
Deflection Temperature at 0.46 MPa (66 psi) 94.4 - 113 °C
202 - 235 °F
Average value: 102 °C Grade Count:8
Deflection Temperature at 1.8 MPa (264 psi) 85.0 - 108 °C
185 - 226 °F
Average value: 97.4 °C Grade Count:14
Vicat Softening Point 95.0 - 240 °C
203 - 464 °F
Average value: 113 °C Grade Count:16
Flammability, UL94 HB
HB
Grade Count:8
Optical Properties Metric English Comments
Refractive Index 1.49 - 1.51
1.49 - 1.51
Average value: 1.49 Grade Count:12
Haze 0.300 - 96.0 %
0.300 - 96.0 %
Average value: 8.90 % Grade Count:12
Yellow Index 0.300 - 5.50 %
0.300 - 5.50 %
Average value: 1.60 % Grade Count:4
Transmission, Visible 80.0 - 93.0 %
80.0 - 93.0 %
Average value: 90.9 % Grade Count:17
Electrical Properties Metric English Comments
Dielectric Strength 18.7 - 20.0 kV/mm
475 - 508 kV/in
Average value: 19.6 kV/mm Grade Count:3
Processing Properties Metric English Comments
Melt Temperature 220 - 250 °C
428 - 482 °F
Average value: 240 °C Grade Count:5
Mold Temperature 43.3 - 90.0 °C
110 - 194 °F
Average value: 65.2 °C Grade Count:5
Drying Temperature 82.2 - 109 °C
180 - 228 °F
Average value: 87.6 °C Grade Count:5