SABIC Innovative Plastics LNP LUBRILOY D20009P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY D20009P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRILOY* D20009P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant, Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ISO 527 |
| 51.0 MPa | 7400 psi | ASTM D638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ASTM D638 |
| 58.0 MPa | 8410 psi | ISO 527 | |
| Elongation at Break | 67.9 % | 67.9 % | ISO 527 |
| 77.4 % | 77.4 % | ASTM D638 | |
| Elongation at Yield | 5.8 % | 5.8 % | ISO 527 |
| 6.2 % | 6.2 % | ASTM D638 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| 2.17 GPa | 315 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 73.0 MPa | 10600 psi | ISO 178 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D790 |
| 2.10 GPa | 305 ksi | ISO 178 | |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 19.75 J/cm | 37.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 172 kJ/m² | 81.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 47.0 J | 34.7 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 48.0 J | 35.4 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.29 | 0.29 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.23 | 0.23 | ASTM D3702 Modified |
| K (wear) Factor | 101 x 10-8 mm³/N-M | 50.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy M25 Wire; 3/4HT (TH03) Temper; 1.3-2.0 mm Diameter (UNS C17300)
- Saint-Gobain CHR® SG36-10(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Blue 4012 Concentrate Based in Polyethylene
- Buckeye Polymers BP FLEX D4107 GO1 BLK Thermoplastic Polyolefin
- ACC SMP™ EP EF SP EPI Engineered Polymers Extra Flex with Silicone
- Americas Styrenics STYRON® 665 High Heat Crystal Polystyrene
- Chosun Refractories HACT-160 High Alumina Castables
- LATI Latimass 53-04 D008 PP Homopolymer, Impact Modified
Copyright © lookpolymers.com All Rights Reserved