SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* OFL36 is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Physical Properties Metric English Comments
Density 1.69 g/cc
0.0611 lb/in³
ASTM D792
1.70 g/cc
0.0614 lb/in³
ISO 1183
Moisture Absorption 0.0100 %
0.0100 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Time 86400 sec
0.0010 - 0.0020 in/in

@Time 24.0 hour
ASTM D955
0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0048 cm/cm

@Time 86400 sec
0.0030 - 0.0048 in/in

@Time 24.0 hour
ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
5 mm/min; ISO 527
124 MPa
18000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.3 %
1.3 %
Type I, 5 mm/min; ASTM D638
1.3 %
1.3 %
5 mm/min; ISO 527
Tensile Modulus 11.99 GPa
1739 ksi
1 mm/min; ISO 527
12.8 GPa
1860 ksi
50 mm/min; ASTM D638
Flexural Strength 178 MPa
25800 psi
1.3 mm/min, 50 mm span; ASTM D790
180 MPa
26100 psi
ISO 178
Flexural Modulus 11.05 GPa
1603 ksi
2 mm/min; ISO 178
11.6 GPa
1680 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.16 J/cm
7.79 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 3.00 J
2.21 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
11.0 J

@Temperature 23.0 °C
8.11 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.44
0.44
ASTM D3702 Modified
Coefficient of Friction, Static 0.35
0.35
ASTM D3702 Modified
K (wear) Factor 14.1 - 16.1 x 10-8 mm³/N-M
7.00 - 8.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
105 x 10-8 mm³/N-M
52.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
25.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
13.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
23.4 - 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.0 - 27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 34.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
18.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
48.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
50.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 278 °C
532 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
278 °C

@Thickness 3.20 mm
532 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 257 °C
495 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
264 °C

@Thickness 3.20 mm
507 °F

@Thickness 0.126 in
unannealed; ASTM D648