Nilit FRIANYL B63 W-KV10 Nylon 6 for injection molding, 10% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 W-KV10 Nylon 6 for injection molding, 10% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0090 - 0.018 cm/cm | 0.0090 - 0.018 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength at Break | 78.0 MPa | 11300 psi | ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/1eU |
| 4.00 J/cm² | 19.0 ft-lb/in² | DIN 53453 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| 0.400 J/cm² | 1.90 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 575 V | 575 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- RheTech Products GC30P200-01 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black
- Radici Radilon® S 37FL T Nylon 6
- Ravago Manufacturing Americas Hylon® N1040MGL Nylon 6/6 (DAM) (discontinued **)
- Momentive Performance Materials RTV12 Clear General Purpose Potting/Encapsulating Compound
- Techmer ES Plastiblend® PA6/ABS 1120 GF15 15% Glass Filled
- Teijin Panlite® K-1300Y Standard (mold release/ice color grade) Polycarbonate Resin
- A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade
- Teknor Apex TruVis Esters™ DIOA Di-IsoOctyl Adipate
- ExxonMobil Escorene™ LD 723.28 Cast Ethylene Vinyl Acetate Copolymer
- DuPont Teijin Films Mylar® EL Polyester Film, 75 Gauge
Copyright © lookpolymers.com All Rights Reserved