SABIC Innovative Plastics LNP VERTON NV006E PC/ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON NV006E PC/ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0011 cm/cm @Time 86400 sec |
0.0011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0052 cm/cm @Time 86400 sec |
0.0052 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 129 MPa | 18700 psi | ASTM D638 |
| 149 MPa | 21600 psi | ISO 527 | |
| Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
| 149 MPa | 21600 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Elongation at Yield | 1.6 % | 1.6 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1 mm/min; ISO 527 |
| 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 122 MPa | 17700 psi | ISO 178 |
| 193 MPa | 28000 psi | ASTM D790 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 2.56 J/cm | 4.80 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 42.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 52.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 52.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N85U Nitrile Rubber
- Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE
- PTS SAN-80HF High Flow SAN Resin
- Huntsman PE1753 EVA Film Extrusion (discontinued **)
- Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17510)
- ITW Devcon Epoxy HP 250, Straw
- A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer
- CP-Polymer-Technik Wellamid® 6000 GV 15 HWCP 15% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Parker Chomerics CHO-BOND 2167 Part B Silicone
Copyright © lookpolymers.com All Rights Reserved