Nilit FRIANYL B63 HS-GV 5 Nylon 6 for injection molding, 5% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 HS-GV 5 Nylon 6 for injection molding, 5% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.011 - 0.020 cm/cm | 0.011 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 95.0 MPa | 13800 psi | ISO 2039-1 |
| Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.20 J/cm² | 29.5 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 7.00 J/cm² @Temperature -40.0 °C |
33.3 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA |
| 1.40 J/cm² | 6.66 ft-lb/in² | DIN 53453 | |
| 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Multibase Nylex™ 1230 Polyamide + PP
- Precision Polymer Engineering V60H Fluoroelastomer Compound
- Lehmann & Voss LUVOCOM® 80-8268 Polyacetal-copolymer, with PTFE, lubricant modified
- Solvay Specialty Polymers Halar® 6014 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
- Hexcel® Redux® 340U(SP) (0.015 psf) Modified epoxy film adhesive for bonding metallic and composite components
- Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets
- ChevronTexaco Dura-Lith® NLGI 000 Grease EP
- China Tungsten YW2A Tungsten Carbide for Cutting Tools
- Westlake EMAC® SP 1205 Ethylene-Methyl Acrylate Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved