SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| 1.05 g/cc | 0.0379 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 1.6 % @Time 86400 sec |
1.6 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0077 cm/cm @Time 86400 sec |
0.0077 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0092 cm/cm @Time 86400 sec |
0.0092 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D 638 |
| 27.0 MPa | 3920 psi | ISO 527 | |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D 638 |
| 36.0 MPa | 5220 psi | ISO 527 | |
| Elongation at Break | 50.1 % | 50.1 % | ISO 527 |
| 52.1 % | 52.1 % | ASTM D 638 | |
| Elongation at Yield | 3.5 % | 3.5 % | ASTM D 638 |
| 3.5 % | 3.5 % | ISO 527 | |
| Tensile Modulus | 1.37 GPa | 199 ksi | 50 mm/min; ASTM D 638 |
| 1.58 GPa | 229 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
| Flexural Modulus | 1.37 GPa | 199 ksi | ASTM D 790 |
| 1.60 GPa | 232 ksi | ISO 178 | |
| Izod Impact, Notched | 3.89 J/cm @Temperature 23.0 °C |
7.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 14.2 J/cm @Temperature 23.0 °C |
26.6 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² @Temperature 23.0 °C |
15.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 148 kJ/m² @Temperature 23.0 °C |
70.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 35.0 J | 25.8 ft-lb | Multiaxial Impact; ISO 6603 |
| 39.0 J @Temperature 23.0 °C |
28.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 127 µm/m-°C @Temperature -40.0 - 40.0 °C |
70.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 128 µm/m-°C @Temperature -40.0 - 40.0 °C |
71.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 103 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 103 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 73.0 °C @Thickness 3.20 mm |
163 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+8 - 1.00e+10 ohm | 1.00e+8 - 1.00e+10 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- ND Industries 306 Surface Insensitive Instant Superglue
- Parker Chomerics CHO-SHIELD® 610 A/B Conductive Epoxy Paint
- EG100A-B40 Polyurethane-based Biomedical Elastomer
- GEHR Plastics PPS-40GF Polyphenylene Sulfide, 40% Glass Fiber
- Lubriplate L0804 Non-Detergent Motor Oil Motor Oil & Transmission Fluid
- SABIC Innovative Plastics LNP STAT-KON EE005E PEI
- Techmer ES HiFill® PET GF20 UV BK 20% Glass Filled
- Samsung Cheil Industries Starex® CM-0140UV ABS, Unreinforced
- Total 3802 B HDPE, cable, sheet, pipe, injection molding
- Arlon SFT 0.012" (0.305 mm) Cured Self-fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved