- Nilit FRIANYL B63 H-SG40 Nylon 6 for injection molding, 40% mineral filled
Nilit FRIANYL B63 H-SG40 Nylon 6 for injection molding, 40% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 H-SG40 Nylon 6 for injection molding, 40% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.014 cm/cm | 0.0080 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 135 MPa | 19600 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers XP23-45 PVC
- Covestro Bayblend® KU2-1500 Polycarbonate + ABS Blend, Extrusion/Blow-Molding (discontinued **)
- Reltek BONDiT™ B-45ESD Adhesive and Sealant
- Mateck GaP
- Sylvin Technologies 8960-75 Natural PVC Extrusion Compound
- A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Dow Corning SYL-OFF® PMCP7673 Coating
- ChevronTexaco TDH® W Oil
- Hippe EP CC 31 Woven Cotton Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod
- California Fine Wire Nickel 211 (Nickel Manganese Alloy)
Copyright © lookpolymers.com All Rights Reserved