Arkema Group Orgalloy® LE 6000T Nylon Alloy, Flexible Grade (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® LE 6000T Nylon Alloy, Flexible Grade (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LE series, flexible polyamide alloys: processable on PE screws, low moisture absorption, chemical resistance (no known solvents).medium viscosity and stiffness, specially suited to the extrusion of film, tube and hollow vessels. Also suited to injection molding. Improved thermal resistance.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³
Water Absorption	6.4 %	6.4 %
Moisture Absorption at Equilibrium	1.8 %	1.8 %	Humidity Absorption
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 235 °C	2.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.0 MPa	5080 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	4.2 %	4.2 %	50 mm/min
Tensile Modulus	1.30 GPa	189 ksi	1 mm/min
Tensile Creep Modulus, 1 hour	1130 MPa	164000 psi
Tensile Creep Modulus, 1000 hours	520 MPa	75400 psi

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Vicat Softening Point	97.0 °C	207 °F	50°C/hr; 50N
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.10 mm	HB @Thickness 0.122 in

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V