- Borealis Nepol™ GB402HP 40% Long Glass Fiber Reinforced Polypropylene
Borealis Nepol™ GB402HP 40% Long Glass Fiber Reinforced Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Borealis |
| Trade Name | Nepol™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Nepol™ GB402HP 40% Long Glass Fiber Reinforced Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nepol GB402HP is a 40% long glass fiber reinforced polypropylene grade, produced using Borealis ` propriety and exclusive, patented Nepol technology intended for injection molding and extrusion. The long glass fibers, chemically coupled to the polypropylene matrix, are providing Nepol GB303HP with outstanding mechanical properties such as high strength, high stiffness and excellent impact resistance.Nepol GB402HP has been designed for front end carriers, structural parts, dashboard carriers, door module carriers, and lead bearing automotive parts.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Borealis Method |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-2 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 5.70 J/cm² | 27.1 ft-lb/in² | ISO 179/1eU |
| 5.50 J/cm² @Temperature -20.0 °C |
26.2 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 2.80 J/cm² | 13.3 ft-lb/in² | ISO 179/1eA |
| 3.20 J/cm² @Temperature -20.0 °C |
15.2 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | ISO 75-2 |
| Vicat Softening Point | 145 °C | 293 °F | B (50N); ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Screw Speed | 30 - 150 rpm | 30 - 150 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fogging, mg | 1.7 | At 100°C/ 16 hours |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE163R PC (Europe-Africa-Middle East)
- LyondellBasell Petrothene® PM92973 Linear Low Density Polyethylene Black Concentrate
- Tipco Tipcolite® TPF 1312 - Unreinforced Thermoset Phenolic Resin, 21 mm Norton Flow with 13% Hexamine
- Diamond Polymers Centrex® 810 Injection Molding Grade
- Arlon Thermabond® 99720W015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- 3M Scotchkote™ 206N XTRA LG Fusion Bonded Epoxy Coating
- Buckeye Polymers BP RPP 0511C Polypropylene, 5% Mineral Filled
- 3M FS532 White Polystyrene Label Products
- PolyOne Synplast™ 810TM-E Tri (n-octyl, n-decyl) Trimellitate
- Polyplastic Armlen® PP MF 20-3-901 Polypropylene, 20% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved