- Solvay TECHNYL® A 218G V33 Black 34N PA66, 25% glass fiber, DRY
Solvay TECHNYL® A 218G V33 Black 34N PA66, 25% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218G V33 Black 34N PA66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 25% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. Available in: Europe and North AmericaProduct Applications: TECHNYL® A 218G1 V25 BLACK 34N is particularly recommended for the injection molding of parts in permanent contact with cooling liquids in cars, such as: - cooling and heating radiator systems, header tanks, thermostat components, inlet / outlet pipes. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183/A |
| Water Absorption | 0.75 % @Temperature 23.0 °C, Time 86400 sec |
0.75 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0108 cm/cm | 0.0108 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0036 cm/cm | 0.0036 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527 Type 1A |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527 Type 1A |
| Tensile Modulus | 10.2 GPa | 1480 ksi | ISO 527 Type 1A |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-(V22) 22 MFI UV Stabilized Polycarbonate With Release
- LG Chemical LUPOL EI5002L PP
- Karina E 105440-35/1-Y-IS-SD-LM Ivory PVC Compound
- Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F)
- LATI Latiohm 66-08 PD02 G/35 PA66, 35% Glass Fiber Reinforced
- Shandong Dongyue Polymer HFC-125 Pentafluoroethane Refrigerant, CHF2CF3
- SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER
- Plastics Group Polifil® RMC-20 20% Calcium Carbonate-Reinforced Polypropylene, High Impact
- DuPont Performance Polymers Hytrel® 8238 Polyester Elastomer TPC-ET (Unverified Data**)
- Braskem PD 943XP HOMO Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved