- Nilit FRIANYL B63 H-GV50 Nylon 6 for injection molding, 50% glass fiber reinforced
Nilit FRIANYL B63 H-GV50 Nylon 6 for injection molding, 50% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 H-GV50 Nylon 6 for injection molding, 50% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 - 2.1 % | 1.2 - 2.1 % | ISO 62 |
| Water Absorption at Saturation | 4.0 - 5.0 % | 4.0 - 5.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0030 - 0.010 cm/cm | 0.0030 - 0.010 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO 2039-1 |
| Tensile Strength at Break | 220 MPa | 31900 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527 |
| Flexural Strength | 310 MPa | 45000 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 5.10 J/cm² @Temperature -40.0 °C |
24.3 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA |
| 1.50 J/cm² | 7.14 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 2024 HS UV 425C Grey Polyamide 66 (Nylon 66)
- Chevron Phillips MarFlex® 7120S LLDPE Blown & Cast Film Resin (discontinued **)
- Taiwan PU Corporation TPU-C75 General Grade, Calender Molding Polyester Base TPU
- Samsung Cheil Industries Starex® WX-9120 ASA, Unreinforced
- Teknor Apex Sinvicomp SIH 5008A Polyvinyl Chloride, Flexible
- CP-Polymer-Technik Wellamid® 6600 GS 20 HWCP 20% Glass Sphere Filled Nylon 66, Heat Stabilized, Dry
- CIMBAR CIMTUFF® 9103s Talc
- 3M Bumpon™ SJ6216 Resilient Rollstock
- BASF Pluracol® 5250 Graft Slabstock Foam Polyol
Copyright © lookpolymers.com All Rights Reserved