- Nilit FRIANYL A63 HS-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
Nilit FRIANYL A63 HS-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 HS-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 - 2.6 % | 1.6 - 2.6 % | ISO 62 |
| Water Absorption at Saturation | 7.0 - 8.0 % | 7.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 102 MPa | 14800 psi | ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO 527 |
| Flexural Strength | 87.0 MPa | 12600 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 3.90 J/cm² @Temperature -40.0 °C |
18.6 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | DIN 53453 |
| 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA | |
| 0.900 J/cm² @Temperature -40.0 °C |
4.28 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant
- Network Polymers Nylon 6040
- Quantum Composites HTC-9590 55% Carbon Fiber Reinforced Bismaleimide SMC, High Temperature Composite
- International Mold Steel Daido DRM1 Matrix High-Speed Steel
- SABIC Innovative Plastics LNP STAT-KON DEL329XF PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP V1000UXC PA
- Epoxy Technology EPO-TEK® E3001-HV Electrically Conductive, Silver Epoxy
- Arlon 51576XC15A 0.015" Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved