PolyOne Stat-Tech™ AS-10SS/000 ABS - 10% Stainless Steel Fiber (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-10SS/000 ABS - 10% Stainless Steel Fiber
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Thickness 3.17 mm |
0.15 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 215 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 100 ohm-cm | 1.0 - 100 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.0 - 100 ohm | 1.0 - 100 ohm | ASTM D257 |
| Shielding Effectiveness | 30 - 60 dB | 30 - 60 dB | 1,000 MHz; PolyOne Internal |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 232 °C | 400 - 450 °F | Molding |
Users viewing this material also viewed the following:
- Piezo Kinetics 556 Lead Zirconate Titanate Piezoelectric
- Victrex® WG101™ Polyaryletherketone
- Sharadaa Ceramics REFINSUL 9 Insulating Castables Medium/High Purity
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.062" thick)
- Saint-Gobain CHR® K109 Polyimide Film Backing Acrylic Adhesive Pressure Sensitive Tape
- A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
- Westlake Plastics Norylux™ Modified Polyphenylene Oxide 30% glass filled
- Bhansali Engineering Santron IMS1000 SAN Resin
- ExxonMobil 797 Mobil DTE 790 Series
- Johnson Matthey JM A5 Soft Solder/Flux
Copyright © lookpolymers.com All Rights Reserved