Diamond Polymers DIAMALOY PC 1008 Impact Modified Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers DIAMALOY PC 1008 Impact Modified Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 3.80 kg, Temperature 200 °C |
8.0 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Break | 117 % | 117 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 85.0 MPa @Thickness 3.17 mm |
12300 psi @Thickness 0.125 in |
chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.205 GPa @Thickness 3.17 mm |
319.8 ksi @Thickness 0.125 in |
chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 7.74 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
14.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 152 °C @Load 1.00 kg, Thickness 3.17 mm |
306 °F @Load 2.20 lb, Thickness 0.125 in |
ASTM D1525 |
Users viewing this material also viewed the following:
- Noltex Soarnol® ET3808 Ethylene Vinyl Alcohol Copolymer
- PolyOne Geon™ Vinyl Flexible R125AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Samsung Cheil Industries Infino® SI-3109GL PC, Glass Filled High Impact
- A. Schulman POLYBATCH™ Tan LL60139/2 Concentrate Based In LLDPE
- Polyplastics Duranex® C5330 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled
- Zeon Chemicals Sivic® Z700PX Polyblend Nitrile Elastomer
- A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene
- DuPont Nucrel® 1202HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
- Eagle Brass 230 Red Brass, Annealed
Copyright © lookpolymers.com All Rights Reserved