Nilit FRIANYL A63 CV-CM 0515 9005/Z Powder-coatable nylon 6.6 for injection molding, 15% ceramic filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 CV-CM 0515 9005/Z Powder-coatable nylon 6.6 for injection molding, 15% ceramic filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Powder-coatable nylon 6.6 for injection molding, with conductive carbon blackInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.1 % | 1.4 - 2.1 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 110 MPa | 16000 psi | ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | ISO 179/1eU |
| 3.70 J/cm² | 17.6 ft-lb/in² | DIN 53453 | |
| 1.60 J/cm² @Temperature -40.0 °C |
7.61 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 2.90 J/cm² @Temperature -30.0 °C |
13.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 | |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| 0.400 J/cm² @Temperature -40.0 °C |
1.90 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Continuous; FRISETTA Test Method |
Users viewing this material also viewed the following:
- ND Industries 360 Surface Insensitive Instant Superglue
- Penn Fibre Pennite® 4512 Nylon 6, 12% Glass Fiber Reinforced (PA6)
- Mallard Creek Polymers ROVENE® 6101 Styrene-Acrylic Emulsion
- SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific)
- Teknor Apex Telcar® OBC 4665A Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Cossa Polimeri ESTASTIR HI 0810 V0 Flame Retardant Polystyrene
- BCC Products BC 8160 Urethane Casting
- Overview of materials for Melamine-Phenolic Copolymer
Copyright © lookpolymers.com All Rights Reserved