Aclo Accutech Polypropylene Homopolymer HP0334T10L1 Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334T10L1 Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.969 g/cc | 0.0350 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ASTM D638 |
| Flexural Strength | 47.0 MPa | 6820 psi | ASTM D790 |
| Flexural Modulus | 2.099 GPa | 304.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.750 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90031 Polyvinyl Chloride, Flexible (PVC, Flexible)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR Plasthall 7050 Plasticizer
- LG Chemical LUTENE FB0300 LDPE Blown Film Grade
- LATI Latene® 7H2W TR/40 PP Homopolymer, Mineral Reinforced, Heat Stabilized
- Master Bond MB302 Cyanoacrylate Adhesive System
- Eagle Brass 240 Low Brass, Extra Hard
- Colorite Polymers 8566 Non-Phthalate 66 Series Vinyl Compound
- ExxonMobil Santoprene® 141-55W185 Thermoplastic Elastomer (discontinued **)
- Hippe PF GC 21 Woven Glass Cloth Reinforced Phenolic Resin - Round, Rolled Tube
Copyright © lookpolymers.com All Rights Reserved