Greene Tweed Arlon® 1330 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced |
| Manufacturer | Greene Tweed |
| Trade Name | Arlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Greene Tweed Arlon® 1330 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprietary manufacturing and machining processes to ensure that Arlons properties consistently outperform the competition.Greene, Tweed offers several different Arlon materials, and all provide high tensile strength and elongation properties, excellent shear strength and creep resistance, outstanding fatigue resistance, broad chemical and radiation resistance, and no susceptibility to hydrolysis (steam/hot water). Our engineers work one on one with customers to find the right solution for each specific application.Information provided by Greene Tweed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Deformation | 0.14 % | 0.14 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 96 | 96 | ASTM D785 |
| Hardness, Shore D | 85 | 85 | ASTM D2240 |
| Tensile Strength at Break | 86.9 MPa | 12600 psi | ASTM D368 |
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21100 psi | ASTM D790 |
| Flexural Modulus | 3.69 GPa | 535 ksi | Flexural 0.5% Secant Modulus; ASTM D790 |
| 0.2031 GPa @Temperature 204 °C |
29.46 ksi @Temperature 400 °F |
||
| Compressive Strength | 107 MPa | 15500 psi | ASTM D695 |
| Shear Strength | 71.7 MPa | 10400 psi | Axial; ASTM D732 |
| 71.7 MPa | 10400 psi | Transverse; ASTM D732 | |
| 14.3 MPa @Temperature 288 °C |
2080 psi @Temperature 550 °F |
||
| 48.7 MPa @Temperature 149 °C |
7070 psi @Temperature 300 °F |
||
| 68.3 MPa @Temperature 65.6 °C |
9900 psi @Temperature 150 °F |
||
| Secant Modulus | 3.59 GPa | 521 ksi | Tensile 0.5% Secant Modulus; ASTM D638 |
| Coefficient of Friction, Dynamic | 0.15 | 0.15 | PV=12600 psi-ft./min.; ASTM G77 |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr | ASTM G77 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 41.4 µm/m-°C @Temperature <=149 °C |
23.0 µin/in-°F @Temperature <=300 °F |
ASTM E228 |
| 148 µm/m-°C @Temperature >=149 °C |
82.0 µin/in-°F @Temperature >=300 °F |
ASTM E228 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 330 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Tan |
Users viewing this material also viewed the following:
- Niagara LaSalle 1213 Cold Finished Steel Bar
- PSM Industries Pacific Sintered Metals Iron F-241-S1 Powdered Metal
- Kazanorgsintez PE2NT74-15 High Density Polyethylene for Blow Molding
- Loxim 830 02C HB Polypropylene Compound, 30% Calcite Filled, Flame Retardant
- SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer (Asia Pacific)
- Sapco C 410 Steatite
- ExxonMobil 20W-50 Exxon Aviation Oil Elite
- Cotronics Resbond™ 950 High Temperature Ceramic Adhesive, Aluminum Composition
- 3M 7811 Dot Matrix Printable Polyimide Label Material
Copyright © lookpolymers.com All Rights Reserved