Multibase Multi-Pro® 2510 XGW Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 2510 XGW Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral Filled, 27% by weight.Features:Gloss, HighForms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.5 MPa | 3410 psi | ASTM D638 |
| Elongation at Break | 220 % | 220 % | ASTM D638 |
| Flexural Yield Strength | 34.5 MPa | 5000 psi | ASTM D790 |
| Flexural Modulus | 1.37 GPa | 199 ksi | ASTM D790 |
| Izod Impact, Notched | 0.577 J/cm | 1.08 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 11.07 J | 8.167 ft-lb | ASTM D3029 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 193 - 232 °C | 380 - 450 °F | |
| Front Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 2-4 tons/in2 | |
| Screw L/D Ratio | 20:1 |
Users viewing this material also viewed the following:
- Raschig Group DECAL® 1760 Phenolic
- Star Plastics PCGF30 Molding Grade PC with 30% Glass
- SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU
- Master Bond EP21SC-1 Two Component Epoxy Resin System
- ThyssenKrupp SECURE 400 Structural Steel
- Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix
- Chem Polymer Chemlon 206 G Nylon 6, 6% Glass Fiber Reinforced
- Radici Radilon® A RV350 (dry) Nylon 66
- LG Chemical XR401F ABS, Heat Resistance
- GEHR Plastics Noryl PPO-30 GF 30% Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved