Lanxess DurethanÂ® BKV 40 H2.0 901510 Nylon 6, Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer	Lanxess
Trade Name	Durethan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lanxess DurethanÂ® BKV 40 H2.0 901510 Nylon 6, Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PA 6, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.

Physical Properties	Metric	English	Comments
Specific Gravity	1.46 g/cc	1.46 g/cc	ISO 1183
Moisture Absorption at Equilibrium	1.8 %	1.8 %	50% RH; ISO 62
Water Absorption at Saturation	6.0 %	6.0 %	ISO 62
Linear Mold Shrinkage, Flow	0.00030 cm/cm	0.00030 in/in	Post-shrinkage, 150x105x3; 120Â°C; 4 hour; ISO 2577
	0.0016 cm/cm	0.0016 in/in	150x105x3; 280Â°C / MT 80Â°C; 400 bar; ISO 2577
Linear Mold Shrinkage, Transverse	0.00070 cm/cm	0.00070 in/in	Post-shrinkage, 150x105x3; 120Â°C; 4 hour; ISO 2577
	0.0085 cm/cm	0.0085 in/in	150x105x3; 280Â°C / MT 80Â°C; 400 bar; ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	cond.; ISO 527-1, -2; 5 mm/min
	195 MPa	28300 psi	d.a.m.; ISO 527-1, -2; 5 mm/min
Tensile Strength, Yield	130 MPa	18900 psi	cond.; ISO 527-1, -2; 50 mm/min
	195 MPa	28300 psi	d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Break	3.0 %	3.0 %	d.a.m.; ISO 527-1, -2; 5 mm/min
	6.0 %	6.0 %	cond.; ISO 527-1, -2; 5 mm/min
Elongation at Yield	3.0 %	3.0 %	d.a.m.; ISO 527-1, -2; 50 mm/min
	6.0 %	6.0 %	cond.; ISO 527-1, -2; 50 mm/min
Tensile Modulus	7.80 GPa	1130 ksi	cond.; ISO 527-1, -2; 1 mm/min
	11.9 GPa	1730 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength	200 MPa @Strain 5.00 %	29000 psi @Strain 5.00 %	cond., 2 mm/min; ISO 178-A
	310 MPa @Strain 4.00 %	45000 psi @Strain 4.00 %	d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength	170 MPa @Strain 3.50 %	24700 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
	305 MPa @Strain 3.50 %	44200 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus	7.30 GPa	1060 ksi	cond., 2 mm/min; ISO 178-A
	11.2 GPa	1620 ksi	d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)	11.0 kJ/mÂ² @Temperature -30.0 Â°C	5.23 ft-lb/inÂ² @Temperature -22.0 Â°F	cond.; ISO 180-1A
	13.0 kJ/mÂ² @Temperature -30.0 Â°C	6.19 ft-lb/inÂ² @Temperature -22.0 Â°F	d.a.m.; ISO 180-1A
	18.0 kJ/mÂ² @Temperature 23.0 Â°C	8.57 ft-lb/inÂ² @Temperature 73.4 Â°F	d.a.m.; ISO 180-1A
	24.0 kJ/mÂ² @Temperature 23.0 Â°C	11.4 ft-lb/inÂ² @Temperature 73.4 Â°F	cond.; ISO 180-1A
Charpy Impact Unnotched	7.00 J/cmÂ² @Temperature -30.0 Â°C	33.3 ft-lb/inÂ² @Temperature -22.0 Â°F	d.a.m.; ISO 179-1eU
	7.00 J/cmÂ² @Temperature -30.0 Â°C	33.3 ft-lb/inÂ² @Temperature -22.0 Â°F	cond.; ISO 179-1eU
	8.50 J/cmÂ² @Temperature 23.0 Â°C	40.4 ft-lb/inÂ² @Temperature 73.4 Â°F	d.a.m.; ISO 179-1eU
	9.00 J/cmÂ² @Temperature 23.0 Â°C	42.8 ft-lb/inÂ² @Temperature 73.4 Â°F	cond.; ISO 179-1eU
Charpy Impact, Notched	1.50 J/cmÂ²	7.14 ft-lb/inÂ²	d.a.m.; ISO 179-1eA
	2.00 J/cmÂ²	9.52 ft-lb/inÂ²	cond.; ISO 179-1eA

Thermal Properties	Metric	English	Comments
Melting Point	222 Â°C	432 Â°F	10Â°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi)	215 Â°C	419 Â°F	ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi)	200 Â°C	392 Â°F	ISO 75-1, -2
Vicat Softening Point	>= 200 Â°C @Load 5.10 kg	>= 392 Â°F @Load 11.2 lb	120Â°C/hour; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Glow Wire Test	650 Â°C @Diameter 2.00 mm	1200 Â°F @Diameter 0.0787 in	GWFI; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	cond.; IEC 60093
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	d.a.m.; IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	cond.; IEC 60093
	1.00e+14 ohm	1.00e+14 ohm	d.a.m.; IEC 60093
Dielectric Constant	4.0 @Frequency 100 Hz	4.0 @Frequency 100 Hz	d.a.m.; IEC 60250
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	d.a.m.; IEC 60250
	5.0 @Frequency 1.00e+6 Hz	5.0 @Frequency 1.00e+6 Hz	cond.; IEC 60250
	10 @Frequency 100 Hz	10 @Frequency 100 Hz	cond.; IEC 60250
Dielectric Strength	35.0 kV/mm @Thickness 1.00 mm	889 kV/in @Thickness 0.0394 in	cond.; IEC 60243-1
	40.0 kV/mm @Thickness 1.00 mm	1020 kV/in @Thickness 0.0394 in	d.a.m.; IEC 60243-1
Dissipation Factor	0.0050 @Frequency 100 Hz	0.0050 @Frequency 100 Hz	d.a.m.; IEC 60250
	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	d.a.m.; IEC 60250
	0.12 @Frequency 1.00e+6 Hz	0.12 @Frequency 1.00e+6 Hz	cond.; IEC 60250
	0.25 @Frequency 100 Hz	0.25 @Frequency 100 Hz	cond.; IEC 60250
Comparative Tracking Index	400 V	400 V	d.a.m.; Solution A; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	270 - 290 Â°C	518 - 554 Â°F
	280 Â°C	536 Â°F	for test specimens; ISO 294
Mold Temperature	80.0 Â°C	176 Â°F	for test specimens; ISO 294
	80.0 - 120 Â°C	176 - 248 Â°F
Drying Temperature	80.0 Â°C	176 Â°F
Dry Time	2 - 6 hour	2 - 6 hour
Moisture Content	0.030 - 0.12 %	0.030 - 0.12 %	residual; Karl Fischer Test

Descriptive Properties	Value	Comments
ISO Shortname	ISO 1874-PA 6, GHR, 14-120, GF40