Lucite International Diakon® Frost 952 80 Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® Frost 952 80 Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ISO 2039-2 |
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 72.0 MPa | 10400 psi | ISO 527 |
| Elongation at Break | 6.4 % | 6.4 % | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.60 kJ/m² | 0.761 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75A |
| Vicat Softening Point | 101 °C | 214 °F | ISO 306B |
| 108 °C | 226 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 88.8 % | 88.8 % | ASTM D1003 |
| Transmission, Visible | 87.3 % | 87.3 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Nylene® Vexel™ B12GF15 FR , 15% Glass Reinforced, Flame Retardant PBT
- DSM Biomedical PurSil® AL 20 Aliphatic Thermoplastic Silicone Polyether Urethane (discontinued **)
- H.C. Starck Grade AX Zirconium Carbide, ZrC
- Borealis LE4201R Polyethylene Insulation Compound, Crosslinkable
- Plastics Group Polifil® GFRMPPCC-20 20% Glass Reinforced Polypropylene, High Impact
- Dow LDPE 494A Low Density Polyethylene, Film Grade
- 3M Novec™ 1710 Electronic Grade Coating
- Unitika ET2025 PA6, Dry
- LATI LASULF G/20 20% Glass Reinforced Polysulfone (PSU) (Unverified Data**)
- Solvay Specialty Polymers Virantage® VW-10700 RP, RFP, RSFP Polyethersulfone (PESU) (Unverified Data**)&l
Copyright © lookpolymers.com All Rights Reserved