Polymer Property : Melt Flow = 1.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	1.5 g/10 min @Load 3.80 kg, Temperature 230 °C	1.5 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D 1238
SABIC Innovative Plastics Cycolac® X17 ABS Automotive: Very high heat resistance with high strength and modulus. UL94 HB rated.This data was supplied by SABIC-IP for the Americas region.
Melt Flow	1.5 g/10 min	1.5 g/10 min	ExxonMobil Method
ExxonMobil Exceed™ 1518CA Tough Premium Film Resin (discontinued **) Exceed 1518CA resin is a hexene copolymer produced using ExxonMobil Chemicals EXXPOL® Technology. Films made from 1518CA resin have outstanding tensile, impact strength and puncture. These superi..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133
DuPont Elvax® 466 Ethylene Vinyl Acetate (discontinued **) DuPont™ Elvax® 466 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Applications:Elvax® 466 resins can be used for the following applications: adhesives, sealants..
Melt Flow	1.5 g/10 min	1.5 g/10 min	Exxon Method
ExxonMobil Escorene® LD-720 High EVA Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer specialty film resin designed for applications requiring outstanding heat sealability along with excellent strength p..
Melt Flow	1.5 - 2.5 g/10 min	1.5 - 2.5 g/10 min
Kazanorgsintez 108-276 Low Density Polyethylene Composition with Improved Processibility Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Melt Flow	1.5 g/10 min	1.5 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA967000 Low Density Polyethylene, Film Extrusion Grade Petrothene NA967000 is a low density polyethylene resin designed for blown film, general purpose and industrial packaging applications. NA967000 exhibits good processing characteristics and impact s..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	1.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
LG Chemical LUPOL GP1007FE Flame Retardant PP Description: Injection Molding, FR PP, General Purpose, Flame RetardantApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 1309-64-4Information provided by LG Chemical
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	1.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133
Kuraray SEPTONÂ® S4030 Thermoplastic Rubber SEPTONÂ® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTONÂ® resins are hydrogenated styrenic block copolymers, which exhi..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	1.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	Condition L; ASTM D1238
LyondellBasell Pro-faxâ„¢ SD183 Polypropylene Copolymer Description: Pro-faxâ„¢ SD183 medium impact polypropylene copolymer resin is extremely resistant to aging at elevated temperatures in both wet and dry environments. It has an excellent balance of..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 Â°C	1.5 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Micropol Isoplas P651 Crosslinkable Polyethylene Information provided by Micropol Limited
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	1.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
Multibase Multi-FlexÂ® A 5904 LC TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Heat StabilizedOzone Resistant Forms:PelletsProcessing Method:Injection Molding Information provided by Multibase
Melt Flow	1.5 g/10 min	1.5 g/10 min	ISO 1133
Solvay Specialty Polymers Catalyst CT 0552/09 Polyolefin Catalyst CT 0552/09 is a PE based catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water..
Melt Flow	1.5 g/10 min	1.5 g/10 min	ASTM D1238
Styrolution PS-168MO Polystyrene Description: Polystyrene 168MO is a high heat, high molecular weight general purpose polystyrene with low residual volatiles, excellent clarity and high melt strength. These properties makes it an e..
Melt Flow	1.5 g/10 min @Load 3.80 kg, Temperature 230 Â°C	1.5 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM D1238
Styron PulseÂ® B-270 PC/ABS Engineering ResinInformation provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Melt Flow	1.5 g/10 min @Load 5.00 kg, Temperature 200 Â°C	1.5 g/10 min @Load 11.0 lb, Temperature 392 Â°F	Condition G; ASTM D1238
Styrolution NASÂ® 90 High Performance Styrenic NASÂ® 90 has sparkling clarity, improved toughness, and good scratch resistance. This easily processed copolymer blends well with clear impact modifiers. It meets USP XXIII Spec. of Class VI Pla..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 °C	1.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Borclear™ RB707CF Polypropylene Random Copolymer for Blown Film Borclear RB707CF is a propylene-ethylene copolymer film resin without slip and antiblock additives, suitable for the manufacturing of unoriented film on blown film process.Borclear RB707CF is especi..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis BorPURE™ MB6562 High Density Polyethylene for Injection Molding BorPure™ MB6562 is a bimodal, high-density polyethylene intended for injection and compression molding. This grade combines excellent organoleptic properties, environmental stress crack resistance ..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis BorPURE™ MB6561 High Density Polyethylene for Injection Molding BorPure™ MB6561 is a bimodal, high-density polyethylene intended for injection and compression molding. This grade combines excellent organoleptic properties, environmental stress crack resistance ..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 °C	1.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis RB607MO Polypropylene Random Copolymer RB607MO is a random copolymer for blow molding, with good transparency and contact clarity, very good gloss and surface finish. Bottles up to 2 liters can be steam sterilized due to heat distortion ..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil Exceed™ 1518HA Metallocene Polyethylene Resin Product Description: Exceed 1518HA is a metallocene ethylene-hexene copolymer. Films made from Exceed 1518HA have outstanding tensile, impact strength and puncture. These superior strength propertie..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil Exceed™ 1518KC Metallocene Polyethylene Resin Product Description: Exceed 1518KC is a metallocene ethylene-hexene copolymer. Films made from Exceed 1518KC have outstanding tensile, impact strength and puncture. These superior strength propertie..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil LDPE LD 368ON Low Density Polyethylene Resin Product Description: LD 368 series are high clarity EVA LDPE grades, offering good optical properties combined with toughness and impact resistance. Two additive combinations are available according..
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 °C	1.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Braskem H 603 Extrusion Polypropylene Homopolymer Flat and corrugated sheets in general.Information provided by Braskem.
Melt Flow	1.5 g/10 min	1.5 g/10 min	ISO 1133
Addiplast Addilene H 140 Polypropylene Homopolymer Unreinforced, low flow for injection and extrusion, very translucentInformation provided by Addiplast.
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 230 °C	1.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Braskem H 604 Thermoforming & Extrusion Polypropylene Homopolymer Transparent packaging for food; Flat and corrugated sheets for school and office folders.Information provided by Braskem.
Melt Flow	1.5 - 3.0 g/10 min @Load 5.00 kg, Temperature 372 °C	1.5 - 3.0 g/10 min @Load 11.0 lb, Temperature 702 °F	ASTM D1238
Solvay Specialty Polymers Hyflon® PFA 420 Perfluoroalkoxy (PFA) (Unverified Data**) Hyflon® PFA is a family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, ..
Melt Flow	1.5 g/10 min @Load 1.20 kg, Temperature 300 °C	1.5 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Amco Amalloy® B1044 Polymer Alloy Amco Amalloy B1044 is a proprietary copolymer with exceptional clarity and toughness.Low haze, low melt flow, high tensile & flexural strength.Information provided by Amco Plastic Materials.
Melt Flow	1.5 g/10 min @Temperature 230 °C	1.5 g/10 min @Temperature 446 °F	Condition L; ASTM D1238
A. Schulman PP 2407 Polypropylene Impact Resistant Copolymer Polypropylene DescriptionPolypropylene PP 2407 is a low flow, impact resistant copolymer polypropylene. Information provided by A. Schulman.
Melt Flow	1.5 g/10 min @Load 3.80 kg, Temperature 230 °C	1.5 g/10 min @Load 8.38 lb, Temperature 446 °F
Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade (discontinued **) OROGLAS V 044 is an extrusion grade offering good compromise between physical properties and thermal resistance.OROGLAS V 044 is recommended for extrusion of profiles, tubes and sheets.ISO data prov..
Melt Flow	1.5 g/10 min	1.5 g/10 min	ASTM D1238
Huntsman PE1353 EVA Film Extrusion (discontinued **) 3.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..