Lucite International Diakon® Frost 902 51 Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® Frost 902 51 Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ISO 2039-2 |
| Ball Indentation Hardness | 180 MPa | 26100 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Strength | 98.0 MPa | 14200 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.30 kJ/m² | 0.619 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.170 J/cm² | 0.809 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75A |
| Vicat Softening Point | 102 °C | 216 °F | ISO 306B |
| 108 °C | 226 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 66 % | 66 % | ASTM D1003 |
| Transmission, Visible | 74 % | 74 % | ASTM D1003 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 1200 A 33 Natural Polyamide 66 (Nylon 66)
- Solvay Specialty Polymers Amodel® AF-1550 V0 Polyphthalamide (PPA) Resin, 50% Glass/Mineral Reinforced, Dry As Molded &
- LG Chemical LUMID HI5006A(W) PA6/ABS, High Impact, Good Dimensional Stability
- Kraton® G1643 M (SEBS) Linear Triblock Copolymer
- Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
- SABIC Innovative Plastics NORYL WCD883 PPE-TPE (Europe-Africa-Middle East)
- Cheng Yu Plastic BK1021 Electric Conducting Polypropylene, Extrusion
- BASF Neopolen® P 8015 0.03 g/cc Core density; Expanded Polypropylene (Europe)
- DuPont Performance Polymers Neoprene TRT Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved